08585 An Examination of the Chromium-Rich Passive Film Formation on Alloy 22 in Mild Alkaline Environments

Picture for 08585 An Examination of the Chromium-Rich Passive Film Formation on Alloy 22 in Mild Alkaline Enviro
Available for download
Product Number: 51300-08585-SG
ISBN: 08585 2008 CP
Author: Todd Mintz, Hipolito Gonzalez, and Yi-Ming Pan
Publication Date: 2008
$0.00
$20.00
$20.00
The passivity of Alloy 22 is attributed to the presence of a chromium-rich oxide film. However, in some alkaline environments, such as simulated concentrated water, a chromium-rich passive film has not been observed. It is believed that the chromium-rich passive film should be present because of the measured low corrosion rates. A silica/carbon contamination layer noted on the surface of Alloy 22 (UNS N06022) could also contribute to the observed low corrosion rates. A thermodynamic analysis was conducted to analyze the formation of the chromium-rich passive film. Solution compositions examined by other investigators where chromium oxides were not detected have been evaluated with commercial software to develop potential-pH diagrams. The thermodynamic data indicate that a chromium-nickel oxide (NiCr2O4) is thermodynamically stable and may be a likely contributor to the observed low corrosion rates. Failure to observe the film is probably due to it being masked by a thick outer layer on the surface in combination with the dimensions of the film.
The passivity of Alloy 22 is attributed to the presence of a chromium-rich oxide film. However, in some alkaline environments, such as simulated concentrated water, a chromium-rich passive film has not been observed. It is believed that the chromium-rich passive film should be present because of the measured low corrosion rates. A silica/carbon contamination layer noted on the surface of Alloy 22 (UNS N06022) could also contribute to the observed low corrosion rates. A thermodynamic analysis was conducted to analyze the formation of the chromium-rich passive film. Solution compositions examined by other investigators where chromium oxides were not detected have been evaluated with commercial software to develop potential-pH diagrams. The thermodynamic data indicate that a chromium-nickel oxide (NiCr2O4) is thermodynamically stable and may be a likely contributor to the observed low corrosion rates. Failure to observe the film is probably due to it being masked by a thick outer layer on the surface in combination with the dimensions of the film.
Product tags
Also Purchased
Picture for 08564 Predicting the Curvature of the Interface for an Oil/Water Flow and its Effects on Corrosion
Available for download

08564 Predicting the Curvature of the Interface for an Oil/Water Flow and its Effects on Corrosion

Product Number: 51300-08564-SG
ISBN: 08564 2008 CP
Author: Chuntao Deng, Keith Adams, and Trevor MacFarlane
Publication Date: 2008
$20.00
Picture for 08579 Anodic and Cathodic Behavior of Mill Annealed and Topologically Closed Packed Alloy 22, in Chl
Available for download

08579 Anodic and Cathodic Behavior of Mill Annealed and Topologically Closed Packed Alloy 22, in Chloride Solutions

Product Number: 51300-08579-SG
ISBN: 08579 2008 CP
Author: Ricardo M. Carranza, Martin A. Rodriguez, and Raul B. Rebak
Publication Date: 2008
$20.00
Picture for 08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow
Available for download

08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow

Product Number: 51300-08572-SG
ISBN: 08572 2008 CP
Author: Joshua Addis, Srdjan Nesic, and Bruce Brown
Publication Date: 2008
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support