07504 Corrosion Fatigue of Cast Aluminum Alloys in Engine Coolant

Picture for 07504 Corrosion Fatigue of Cast Aluminum Alloys in Engine Coolant
Available for download
Product Number: 51300-07504-SG
ISBN: 07504 2007 CP
Author: Thomas L. Ladwein, Ralf Ripberger, and Cristian Stolze
Publication Date: 2007
$0.00
$20.00
$20.00
Corrosion fatigue tests were performed on three cast aluminium alloys in engine coolant using a revolving bending test apparatus. A decrease in the bearable load is detected for the tests under corrosive conditions compared to standard fatigue testing in air. The surface condition of the test specimens showed a remarkable influence, whereby specimens with a machined surface failed earlier than those with as-cast surface condition. Electrochemical noise measurements could be used to detect the early stages of failure.
Corrosion fatigue tests were performed on three cast aluminium alloys in engine coolant using a revolving bending test apparatus. A decrease in the bearable load is detected for the tests under corrosive conditions compared to standard fatigue testing in air. The surface condition of the test specimens showed a remarkable influence, whereby specimens with a machined surface failed earlier than those with as-cast surface condition. Electrochemical noise measurements could be used to detect the early stages of failure.
Product tags
Also Purchased
Picture for Localized Corrosion of Aluminum Alloy 5052 for Desalination Service
Available for download

Localized Corrosion of Aluminum Alloy 5052 for Desalination Service

Product Number: 51317--9151-SG
ISBN: 9151 2017 CP
Author: Mariano Kappes
Publication Date: 2017
$20.00

Seawater desalination with waste heat from nuclear or fossil power plants is an attractive alternative for the production of potable water.1 Multi-effect desalination process (MED) relies on the evaporation of water from a thin film of seawater.2 The heat of condensation is used in the evaporation of water from a subsequent film of seawater.
Picture for 96260 THE EFFECT OF PRE-EXISTING CORROSION
Available for download

96260 THE EFFECT OF PRE-EXISTING CORROSION ON THE FATIGUE CRACKING BEHAVIOR OF ALUMINUM ALLOYS

Product Number: 51300-96260-SG
ISBN: 96260 1996 CP
Author: E.L. Hagerdorn, G.H. Koch
$20.00
Picture for Documented Evidence of Significant Metal Loss in Aluminum Crevice Corrosion
Available for download

51316-7199-Documented Evidence of Significant Metal Loss in Aluminum Crevice Corrosion

Product Number: 51316-7199-SG
ISBN: 7199 2016 CP
Author: Brian DeForce
Publication Date: 2016
$20.00

The crevice corrosion of aluminum (99.999 wt. %) in neutral and mildly acidic solutions was investigated. Polarization curves were generated in simulated crevice solutions and potentiostatic crevice corrosion experiments with varying crevice gaps were performed.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support