It is today well known that low temperature creep or relaxation plays an impoftant role in the failure
mechanism for hydrogen embrittlement of duplex stainless steel subject to cathodic protection.
Avoiding low temperature creep or relaxation during service has been one important principle in recent
design recommendations in order to avoid hydrogen embrittlement.