07297 PERFORMANCE OF CONCRETE COATINGS AGAINST CARBONATION-INDUCED CORROSION

Picture for 07297 PERFORMANCE OF CONCRETE COATINGS AGAINST CARBONATION-INDUCED CORROSION
Available for download
Product Number: 51300-07297-SG
ISBN: 07297 2007 CP
Author: Eric I. Moreno, Rómel G. Solís-Carcaño, Daniel Serrano-Ixtepan, and César A. Arias-Palma
Publication Date: 2007
$0.00
$20.00
$20.00
Concrete carbonation, as long as chloride ion, is the main cause of corrosion in reinforced concrete structures. Away from marine environments, carbonation-induced corrosion would be the corrosion mechanism in reinforced concrete. After carbonation occurred, plain reinforcing steel bars are known to corrode actively. The objective of this investigation was to study the performance of concrete coatings as an alternative to avoid carbonation of concrete elements, and therefore, corrosion of the reinforcement. Two different coatings (vynil-acrylic and acrylic) were employed in concrete specimens to monitor the carbonation progress. Concrete specimens were cylindrical in shape, cast using three water/cement ratios. The specimens were carbonated in an accelerated carbonation chamber at 4% CO2 and 60% RH. The results indicated that the acrylic and good-quality vinyl-acrylic coatings successfully reduced the carbonation rate of the concrete specimens; regular- and low-quality vinyl-acrylic coatings did not reduced the carbonation rate. Acrylic coatings may be a good material to prevent further concrete carbonation under inland tropical environments.
Concrete carbonation, as long as chloride ion, is the main cause of corrosion in reinforced concrete structures. Away from marine environments, carbonation-induced corrosion would be the corrosion mechanism in reinforced concrete. After carbonation occurred, plain reinforcing steel bars are known to corrode actively. The objective of this investigation was to study the performance of concrete coatings as an alternative to avoid carbonation of concrete elements, and therefore, corrosion of the reinforcement. Two different coatings (vynil-acrylic and acrylic) were employed in concrete specimens to monitor the carbonation progress. Concrete specimens were cylindrical in shape, cast using three water/cement ratios. The specimens were carbonated in an accelerated carbonation chamber at 4% CO2 and 60% RH. The results indicated that the acrylic and good-quality vinyl-acrylic coatings successfully reduced the carbonation rate of the concrete specimens; regular- and low-quality vinyl-acrylic coatings did not reduced the carbonation rate. Acrylic coatings may be a good material to prevent further concrete carbonation under inland tropical environments.
Product tags
Also Purchased
Picture for 96339 PHENOMENA THAT DISTURB THE MEASUREMENT
Available for download

96339 PHENOMENA THAT DISTURB THE MEASUREMENT OF POTENTIALS IN CONCRETE

Product Number: 51300-96339-SG
ISBN: 96339 1996 CP
Author: Roar Myrdal
$20.00
Picture for 11003 Modelling the Rate of Deterioration of Reinforced Concrete Structures
Available for download

11003 Modelling the Rate of Deterioration of Reinforced Concrete Structures

Product Number: 51300-11003-SG
ISBN: 11003 2011 CP
Author: John Broomfield
Publication Date: 2011
$20.00
Picture for 07279 PROTECTION OF REINFORCED CONCRETE STRUCTURES IN CHLORIDE-SULFATE EXPOSURES
Available for download

07279 PROTECTION OF REINFORCED CONCRETE STRUCTURES IN CHLORIDE-SULFATE EXPOSURES

Product Number: 51300-07279-SG
ISBN: 07279
Author: Omar Saeed Baghabra Al-Amoudi
Publication Date: 2007
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support