07110 Effect of High Pressure Methane on Stress Corrosion Susceptibility of Casing Steels

Picture for 07110 Effect of High Pressure Methane on Stress Corrosion Susceptibility of Casing Steels
Available for download
Product Number: 51300-07110-SG
ISBN: 07110 2007 CP
Author: Peter R. Rhodes, Lillian Skogsberg, Russell D. Kane, Elizabeth A. Trillo, and R. Schofield
Publication Date: 2007
$0.00
$20.00
$20.00
Thermodynamic calculations show that the H2S solubility in aqueous solution, at a given H2S partial pressure, will be significantly reduced, compared to ambient pressure values, when exposed to high pressure CH4. This reduced H2S solubility suggests that current laboratory-based limits on the H2S partial pressure, PH2S, may be excessively high for use of low alloys steels and corrosion resistant alloys in high pressure gas and oil wells. Laboratory tests at lower PH2S, but with the aim of matching the H2S concentration to the calculated field value, have been proposed. The results of laboratory tests designed to verify this proposal have been made. The calculated decrease in the solubility of H2S at 341 bar (5000 psi) CH4 was confirmed. Two tests with low alloy steel confirmed some benefit, but less than projected. A test with a martensitic stainless steel showed no benefit. Experimental parameters that may have influenced these test results are identified.
Thermodynamic calculations show that the H2S solubility in aqueous solution, at a given H2S partial pressure, will be significantly reduced, compared to ambient pressure values, when exposed to high pressure CH4. This reduced H2S solubility suggests that current laboratory-based limits on the H2S partial pressure, PH2S, may be excessively high for use of low alloys steels and corrosion resistant alloys in high pressure gas and oil wells. Laboratory tests at lower PH2S, but with the aim of matching the H2S concentration to the calculated field value, have been proposed. The results of laboratory tests designed to verify this proposal have been made. The calculated decrease in the solubility of H2S at 341 bar (5000 psi) CH4 was confirmed. Two tests with low alloy steel confirmed some benefit, but less than projected. A test with a martensitic stainless steel showed no benefit. Experimental parameters that may have influenced these test results are identified.
Product tags
Also Purchased
Picture for 07112 Evaluation of Fitness for Purpose Test Environments for Sulfide Stress Cracking Tests of Casin
Available for download

07112 Evaluation of Fitness for Purpose Test Environments for Sulfide Stress Cracking Tests of Casing Steels

Product Number: 51300-07112-SG
ISBN: 07112 2007 CP
Author: Peter R. Rhodes, Lillian Skogsberg, W.H. Grimes, Russell D.Kane, and Elizabeth A. Trillo
Publication Date: 2007
$20.00
Picture for 07079 SIGNIFICANCE OF HYDROGEN EVOLUTION DURING CATHODIC PROTECTION
Available for download

07079 SIGNIFICANCE OF HYDROGEN EVOLUTION DURING CATHODIC PROTECTION

Product Number: 51300-07079-SG
ISBN: 07079 2007 CP
Author: Trine Okstad, Øyvind Rannestad, Roy Johnsen, and Kemal Nisancioglu
Publication Date: 2007
$20.00
Picture for 07091 Effect of Alloying Element on Intergranular Stress Corrosion Cracking Susceptibility of Super
Available for download

07091 Effect of Alloying Element on Intergranular Stress Corrosion Cracking Susceptibility of Super Martensitic Stainless Steel Welded Joints in Sweet Environment

Product Number: 51300-07091-SG
ISBN: 07091 2007 CP
Author: Hisashi Amaya, Kazuhiro Ogawa, Akira Taniyama, and Masakatsu Ueda
Publication Date: 2007
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support