06041 MECHANICAL ASPECTS OF ANTI-CORROSIVE COATINGS PERFORMANCE TESTS

Picture for 06041 MECHANICAL ASPECTS OF ANTI-CORROSIVE
Available for download
Product Number: 51300-06041-SG
ISBN: 06041 2006 CP
Author: Alex A. Volinsky
$0.00
$20.00
$20.00

Protective coating corrosion failure is a complicated process that involves various phenomena which are hard to test for separately. An adequately protected pipe can be in service for a relatively long time without exhibiting any signs of corrosion failure, and then all of a sudden it corrodes over a short period of time. Failure will definitely happen if the interface between the pipe surface and its protective coating system is somehow compromised or exposed to the environment. While corrosion reactions have quite a bit of variability in terms of time, the situation is further complicated when corrosion is coupled with the protective coating mechanical failure. Similar to materials fracture, corrosion failures are governed by the laws of probability, where multiple variables control the ultimate outcome. The coating system needs to be adequately tested before placing it in service, so there is a strong need for a meaningful corrosion test. A typical test would incorporate exposing scratched coating surface to certain corrosive environments for a fixed amount of time, trying to simulate the real conditions as close as possible. Sometimes, a so-called “freeze” step is introduced to “stress” the coating prior to exposing it to the test environment, ultimately causing its failure. Due to the differences in thickness, elastic, thermal and adhesion properties, various coatings would exhibit different results when exposed to a fixed freeze temperature. One needs to understand the mechanics of the freeze in order to properly utilize it. This paper considers the coating delamination and fracture mechanics, including the freeze step mechanics in terms of the strain energy release rate, and coating sub-critical debonding. This research is sponsored by the NACE University Research Seed Grant.

Key Words: Anti-Corrosive Performance Tests, Thermal Cycling, Freeze Step, Fracture Mechanics.

Protective coating corrosion failure is a complicated process that involves various phenomena which are hard to test for separately. An adequately protected pipe can be in service for a relatively long time without exhibiting any signs of corrosion failure, and then all of a sudden it corrodes over a short period of time. Failure will definitely happen if the interface between the pipe surface and its protective coating system is somehow compromised or exposed to the environment. While corrosion reactions have quite a bit of variability in terms of time, the situation is further complicated when corrosion is coupled with the protective coating mechanical failure. Similar to materials fracture, corrosion failures are governed by the laws of probability, where multiple variables control the ultimate outcome. The coating system needs to be adequately tested before placing it in service, so there is a strong need for a meaningful corrosion test. A typical test would incorporate exposing scratched coating surface to certain corrosive environments for a fixed amount of time, trying to simulate the real conditions as close as possible. Sometimes, a so-called “freeze” step is introduced to “stress” the coating prior to exposing it to the test environment, ultimately causing its failure. Due to the differences in thickness, elastic, thermal and adhesion properties, various coatings would exhibit different results when exposed to a fixed freeze temperature. One needs to understand the mechanics of the freeze in order to properly utilize it. This paper considers the coating delamination and fracture mechanics, including the freeze step mechanics in terms of the strain energy release rate, and coating sub-critical debonding. This research is sponsored by the NACE University Research Seed Grant.

Key Words: Anti-Corrosive Performance Tests, Thermal Cycling, Freeze Step, Fracture Mechanics.

PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 06012 TANK LINING COATING SELECTION
Available for download

06012 TANK LINING COATING SELECTION BASED ON LABORATORY TESTS

Product Number: 51300-06012-SG
ISBN: 06012 2006 CP
Author: Amal Al-Borno,Mick Brown, Scott Oliphant
$20.00
Picture for 05021 A Critical Review of Current Performance
Available for download

05021 A Critical Review of Current Performance Tests for Offshore Anti-Corrosive Coatings

Product Number: 51300-05021-SG
ISBN: 05021 2005 CP
Author: David Claydon, International Paints UK; Michael J. Mitchell and Darren Ward, International Protectiv
Publication Date: 2005
$20.00

This paper will critically review the current philosophies described in  ISO and NACE anti-corrosive performance test standards, taking into consideration correlation with natural exposure, track record, validity of "acceptance" or "pre-qualification criteria", dry film thickness and suggested areas for improvement.
Picture for 06030 ANTI-FOULING SILICONE ELASTOMERS
Available for download

06030 ANTI-FOULING SILICONE ELASTOMERS FOR OFFSHORE STRUCTURES

Product Number: 51300-06030-SG
ISBN: 06030 2006 CP
Author: Claus E. Weinell, Jan Roll, Nicholas Marsh
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support