In context of acceptability of 17-4 PH in sour service, an literature survey of complex metallurgy of this grade was done following a mechanical rupture in service. In addition, three 17-4 PH materials were studied in terms of microstructure, mechanical properties and susceptibility to sulfide stress cracking.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Use this error code for reference:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
This paper presents a failure of a material that was overloaded during testing although the raw material was approved based on certified mechanical properties. The failure was due to unsuitable microstructures.
A series of NACE TM0177 Tensile Test Method A tests were conducted on various commercially available chromium-manganese austenitic stainless steels as well as 17-4PH in the 110ksi-to-130ksi yield strength range (34 - 35 HRC max).