03686 FLUORIDE CORROSION OF TI-GRADE 7: EFFECTS OF OTHER IONS

Picture for 03686 FLUORIDE CORROSION OF TI-GRADE 7:

Available for download

Product Number: 51300-03686-SG

ISBN: 03686 2003 CP

Author: A.L. Pulvirenti, K.M. Needham, D. S. Wong, M.A. Adel-Hadadi, A Barkatt, C.R. Marks and J.A. Gorman

Member Price: $0.00

Non Member Price: $20.00

Price: $20.00

Qty:

The effects of chloride, sulfate, and nitrate on the fluoride ion local attack of Ti-Grade 7 (Ti-7: UNS R52400) were investigated. It was observed that the most severe local attack on Ti-7 occurred at approximately 120°C, and at neutral pH. A large chloride: fluoride ratio (10 : 1 by mole) was necessary to produce visible severe attack in immersion tests, but electrochemical studies detected a narrowing of the passive region at chloride: fluoride ratios as small as 1.1 : 1 by mole. The addition of large amounts of sulfate slowed, but did not inhibit pitting and stress corrosion cracking of Ti-7 U-bends, but the addition of nitrate is suspected to act as an effective inhibitor. Polishing of the titanium surface to micron scale also decreased the likelihood of the initiation of local attack.

Overview

The effects of chloride, sulfate, and nitrate on the fluoride ion local attack of Ti-Grade 7 (Ti-7: UNS R52400) were investigated. It was observed that the most severe local attack on Ti-7 occurred at approximately 120°C, and at neutral pH. A large chloride: fluoride ratio (10 : 1 by mole) was necessary to produce visible severe attack in immersion tests, but electrochemical studies detected a narrowing of the passive region at chloride: fluoride ratios as small as 1.1 : 1 by mole. The addition of large amounts of sulfate slowed, but did not inhibit pitting and stress corrosion cracking of Ti-7 U-bends, but the addition of nitrate is suspected to act as an effective inhibitor. Polishing of the titanium surface to micron scale also decreased the likelihood of the initiation of local attack.

PRICE BREAKS - The more you buy, the more you save

Quantity

1+

5+

Price

$20.00

$20.00

Product tags

Also Purchased

Picture for 03682 LOCALIZED CORROSION SUSCEPTIBILITY OF NICKEL

Available for download

03682 LOCALIZED CORROSION SUSCEPTIBILITY OF NICKEL ALLOYS IN HALIDE CONTAINING ENVIRONMENTS

Product Number: 51300-03682-SG

ISBN: 03682 2003 CP

Author: Nacéra S. Meck, Paul Crook, S. Daniel Day, Raúl B. Rebak

$20.00

Picture for 03687 ON APPARENT BI-LINEAR CORROSION RATE

Available for download

03687 ON APPARENT BI-LINEAR CORROSION RATE BEHAVIOR OF TI GRADE 7 IN BASIC SATURATED WATER (BSW-12) BELOW AND ABOVE 80°C

Product Number: 51300-03687-SG

ISBN: 03687 2003 CP

Author: Fred Hua, Gerald Gordon

$20.00

Picture for 03690 EFFECT OF MEASUREMENT METHODS AND SOLUTION

Available for download

03690 EFFECT OF MEASUREMENT METHODS AND SOLUTION CHEMISTRY ON THE EVALUATION OF THE LOCALIZED CORROSION OF CANDIDATE HIGH-LEVEL WASTE CONTAINER MATERIALS

Product Number: 51300-03690-SG

ISBN: 03690 2003 CP

Author: Vijay Jain, Darrell Dunn, Narasi Sridhar, and Lietai Yang

$20.00

Recently viewed

Popular tags

View all