03526 EFFECT OF PROTECTIVE COATINGS ON THE STRESS CORROSION CRACKING OF API 5L-X52 LOW CARBON STEEL IN SOIL AND NS4 SOLUTIONS

Picture for 03526 EFFECT OF PROTECTIVE COATINGS ON
Available for download
Product Number: 51300-03526-SG
ISBN: 03526 2003 CP
Author: J. J.Gonzfilez, Leticia Mejfa
$0.00
$20.00
$20.00
The stress corrosion cracking (SCC) behavior of API 5L-X52 low carbon steel has been studied in a presence of different soil solutions, including synthetic NS4 solutions, with and without barrier coatings using slow strain rate tests (SSRT). The coatings used were a multiple layer system (polyethylene, asphalt resin and epoxy resin) and FBE (fusion bonding epoxy). Results from this study indicate that API 5L-X52 is not susceptible to SCC in soils and NS4 solutions at open corrosion potentials when the FBE and the three layer (3-L) coating were used. However, there is some indication of embrittlement and shows susceptibility at - 1.0 V vs. SCE applied potentials with for the 3-L system in NS4 soil solution and FBE in both environment.
The stress corrosion cracking (SCC) behavior of API 5L-X52 low carbon steel has been studied in a presence of different soil solutions, including synthetic NS4 solutions, with and without barrier coatings using slow strain rate tests (SSRT). The coatings used were a multiple layer system (polyethylene, asphalt resin and epoxy resin) and FBE (fusion bonding epoxy). Results from this study indicate that API 5L-X52 is not susceptible to SCC in soils and NS4 solutions at open corrosion potentials when the FBE and the three layer (3-L) coating were used. However, there is some indication of embrittlement and shows susceptibility at - 1.0 V vs. SCE applied potentials with for the 3-L system in NS4 soil solution and FBE in both environment.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03527 CORROSION FATIGUE AND NEAR-NEUTRAL
Available for download

03527 CORROSION FATIGUE AND NEAR-NEUTRAL pH STRESS CORROSION CRACKING OF PIPELINE STEEL IN VERY DILUTE CARBONATE/BICARBONATE WITH AND WITHOUT THE PRESENCE OF HYDROGEN SULFIDE USING THE COMPLIANCE

Product Number: 51300-03527-SG
ISBN: 03527 2003 CP
Author: R.L. Eadie, K.E. Szklarz, R.L. Sutherby
$20.00
Picture for 03525 IMPROVED TEST METHOD FOR ANALYSIS OF SOHIC-
Available for download

03525 IMPROVED TEST METHOD FOR ANALYSIS OF SOHIC- AND NNSCC SUSCEPTIBILITY TO CRACKING BY CYCLIC LOADING

Product Number: 51300-03525-SG
ISBN: 03525 2003 CP
Author: T. Evertz, V. Flaxa
$20.00
Picture for 10059 Using Soil Analysis and Corrosion Rate Modeling to Support ECDA and Integrity Management
Available for download

10059 Using Soil Analysis and Corrosion Rate Modeling to Support ECDA and Integrity Management of Pipelines and Buried Plant Piping

Product Number: 51300-10059-SG
ISBN: 10059 2010 CP
Author: Stephen F. Biagiotti, Steve Biles and Craig Chaney
Publication Date: 2010
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support