03262 EFFECT OF COMPOSITION AND MICROSTRUCTURE ON THE SEAWATER CORROSION RESISTANCE OF NICKEL-ALUMINUM BRONZE

Picture for 03262 EFFECT OF COMPOSITION AND MICROSTRUCTURE
Available for download
Product Number: 51300-03262-SG
ISBN: 03262 2003 CP
Author: Harold T. Michels, Robert M. Kain
$0.00
$20.00
$20.00
Experimental-size specimens of two different compositions of nickel-aluminum bronze were cast, subjected to five different heat treatments and were exposed to seawater. Both alloys were in compliance with UNS C95800 and MIL-B -244 80, except that the aluminum content of one alloy, at 8.1%, was below the lower limit of the specified compositional range. Their microstructures were characterized and correlated with corrosion resistance. Selective phase attack was seen in both alloys, although it was much more pronounced in the alloy with the lower aluminum content, to the point where entire grains fell out. It was observed that the higher aluminum-containing alloy had markedly superior corrosion resistance. Thus it is important to maintain the aluminum level in alloy UNS C95800 at or above the lower limit, and within the specified range of 8.5-9.5%. Keywords: Aluminum Bronze, Nickel-Aluminum Bronze, Seawater, Microstructure, Martensite, Bainite, Eutectoid, Alpha, Widmanstatten, Phase, Corrosion, Localized Corrosion, Selective Phase Corrosion, Selective Attack, Depth of Attack, Depth of Penetration, UNS C95800, MIL-B-24480.
Experimental-size specimens of two different compositions of nickel-aluminum bronze were cast, subjected to five different heat treatments and were exposed to seawater. Both alloys were in compliance with UNS C95800 and MIL-B -244 80, except that the aluminum content of one alloy, at 8.1%, was below the lower limit of the specified compositional range. Their microstructures were characterized and correlated with corrosion resistance. Selective phase attack was seen in both alloys, although it was much more pronounced in the alloy with the lower aluminum content, to the point where entire grains fell out. It was observed that the higher aluminum-containing alloy had markedly superior corrosion resistance. Thus it is important to maintain the aluminum level in alloy UNS C95800 at or above the lower limit, and within the specified range of 8.5-9.5%. Keywords: Aluminum Bronze, Nickel-Aluminum Bronze, Seawater, Microstructure, Martensite, Bainite, Eutectoid, Alpha, Widmanstatten, Phase, Corrosion, Localized Corrosion, Selective Phase Corrosion, Selective Attack, Depth of Attack, Depth of Penetration, UNS C95800, MIL-B-24480.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 04294 Corrosion Assessment of Nickel Aluminum
Available for download

04294 Corrosion Assessment of Nickel Aluminum Bronze (NAB) in Seawater

Product Number: 51300-04294-SG
ISBN: 04294 2004 CP
Author: Kunigahalli L. Vasanth and Richard A. Hays, Naval Surface Warfare Center
$20.00
Picture for 04301 The Environmental Factors Affecting the
Available for download

04301The Environmental Factors Affecting the Performance of Nickel Aluminum Bronze

Product Number: 51300-04301-SG
ISBN: 04301 2004 CP
Author: Rakesh C. Barik, J.A. Wharton, and Robert J.K. Wood, University of Southampton; K.R. Stokes, Winfrit
$20.00
Picture for Service Performance of Ni-Al Bronze in Marine Environments
Available for download

Service Performance of Ni-Al Bronze in Marine Environments

Product Number: 51317--9298-SG
ISBN: 9298 2017 CP
Author: Moavin Islam
Publication Date: 2017
$20.00

This paper will present two case studies of pre-mature failure of process equipment in seawater service which will illustrate the influence of metallurgical structure on the service performance of Nickel-Aluminum Bronze in marine environments.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support