03115 AN UNUSUAL SULFIDE STRESS CRACKING FAILURE OF A NORTHERN GAS PIPELINE

Product Number: 51300-03115-SG
ISBN: 03115 2003 CP
Author: Karol Szklarz, Erik Haycock, Colin McGovern
$0.00
$20.00
$20.00
A sour gas-gathering pipeline, located in northern Canada, failed by sulfide stress cracking in the body of the pipe. The low strength pipeline was designed and constructed for sour service. The cause of the failure was excessive stress largely due to ice build-up from a nearby ice-road. Numerous cracks and colonies of cracks formed on the internal pipe surface because of high stress. These cracks grew in stages related to the build-up of ice during winter. Keywords: Sulfide Stress Cracking, SSC, Failure Analysis, Carbon Steel, Pipeline, High Stress, Sour Natural Gas.
A sour gas-gathering pipeline, located in northern Canada, failed by sulfide stress cracking in the body of the pipe. The low strength pipeline was designed and constructed for sour service. The cause of the failure was excessive stress largely due to ice build-up from a nearby ice-road. Numerous cracks and colonies of cracks formed on the internal pipe surface because of high stress. These cracks grew in stages related to the build-up of ice during winter. Keywords: Sulfide Stress Cracking, SSC, Failure Analysis, Carbon Steel, Pipeline, High Stress, Sour Natural Gas.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99428 Sulfide Stress Cracking of a Pipeline
Available for download

99428 Sulfide Stress Cracking of a Pipeline Weld in Sour Gas Service

Product Number: 51300-99428-SG
ISBN: 99428 1999 CP
Author: K. E. Szklarz
$20.00
Picture for 08480 Sulfide Stress Cracking of Pipeline - Case History
Available for download

08480 Sulfide Stress Cracking of Pipeline - Case History

Product Number: 51300-08480-SG
ISBN: 08480 2008 CP
Author: Daryoush Masouri, Mahmoud Zafari, and Amir Araghi
Publication Date: 2008
$20.00
Picture for 11105 Sulfide Stress Cracking Susceptibility of Local Hard Areas in Carbon Steel Weld Heat Affected
Available for download

11105 Sulfide Stress Cracking Susceptibility of Local Hard Areas in Carbon Steel Weld Heat Affected

Product Number: 51300-11105-SG
ISBN: 11105 2011 CP
Author: Ben Crowder, James Buchanan, Sam Mishael, and Ron Shockley
Publication Date: 2011
$20.00