02374 High Temperature Corrosion Mechanisms by Combustion Products of Heavy High Sulphur Fuel Oils: An Extension of the Wilson Model

Picture for 02374 High Temperature Corrosion Mechanisms...
Available for download
Product Number: 51300-02374-SG
ISBN: 02374 2002 CP
Author: A. Wong-Moreno, D. Lopez-Lopez, and L. Martinez
$0.00
$20.00
$20.00
Metallic dissolution caused by molten vanadates has been classically considered the main corrosion process involved in the degradation of alloys exposed to the combustion products of heavy fuel oils. However, residual oils used today have higher sulfur contents, and field and laboratory studies have shown that alloys exposed at elevated temperatures to their combustion products experience a more complex corrosion process. High temperature oil ash corrosion involves, besides the occurrence of vanadium corrosion, accelerated oxidation, sulfidation and carburization, depending on temperature, local atmosphere and ash composition. Wilson proposed a model for the transport, through the corrosion product scale, of species leading to metallic dissolution by molten vanadates. An extension to this model is proposed in order to include the transport of sulfur and oxygen through the scale and into the metal for including internal oxidation and sulfidation. This proposal has been validated by previously published results of a comprehensive corrosion testing of different alloys using real oil ashes and analytical results of corroded specimens carried out by the authors. Key words: oil-ash corrosion, sulfidation, metallic dissolution, oxidation, corrosion mechanisms, high temperature.
Metallic dissolution caused by molten vanadates has been classically considered the main corrosion process involved in the degradation of alloys exposed to the combustion products of heavy fuel oils. However, residual oils used today have higher sulfur contents, and field and laboratory studies have shown that alloys exposed at elevated temperatures to their combustion products experience a more complex corrosion process. High temperature oil ash corrosion involves, besides the occurrence of vanadium corrosion, accelerated oxidation, sulfidation and carburization, depending on temperature, local atmosphere and ash composition. Wilson proposed a model for the transport, through the corrosion product scale, of species leading to metallic dissolution by molten vanadates. An extension to this model is proposed in order to include the transport of sulfur and oxygen through the scale and into the metal for including internal oxidation and sulfidation. This proposal has been validated by previously published results of a comprehensive corrosion testing of different alloys using real oil ashes and analytical results of corroded specimens carried out by the authors. Key words: oil-ash corrosion, sulfidation, metallic dissolution, oxidation, corrosion mechanisms, high temperature.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99071 HIGH TEMPERATURE CORROSION OF FUEL OIL
Available for download

99071 HIGH TEMPERATURE CORROSION OF FUEL OIL BURNER COMPONENTS

Product Number: 51300-99071-SG
ISBN: 99071 1999 CP
Author: B. Campillo, L. Martinez, D. Lopez-Lopez, J. Castrejon and A. Wong-Moreno
$20.00
Picture for Accelerated Corrosion of 304H SS in RFCC Regenerators Involving Low Temperature Eutectic-Forming Sal
Available for download

Accelerated Corrosion of 304H SS in RFCC Regenerators Involving Low Temperature Eutectic-Forming Salts

Product Number: 51317--8915-SG
ISBN: 8915 2017 CP
Author: Jayant Nair
Publication Date: 2017
$20.00

This article presents findings on type II high temperature (650-800ºC) corrosion in Residue Fluid Catalytic cracking (RFCC) regenerator service (alloy SS304H) and examines the possible strategies for alloy upgrade in RFCC service.
Picture for 09358 Corrosion Mitigation and Monitoring in Sulfur Recovery Unit
Available for download

09358 Corrosion Mitigation and Monitoring in Sulfur Recovery Unit

Product Number: 51300-09358-SG
ISBN: 09358 2009 CP
Author: Salah I. Al-Luqman, Majed M. Al-Qarni and Iyad Buraiki
Publication Date: 2009
$20.00

This paper will demonstrate the fundamental corrosion issues encountered in Sulfur Recovery Units. It will address the Claus process chronic corrosion problems such as sulfidation, sour environment cracking, weak acid corrosion, etc.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support