02209 CAVITATION CORROSION BEHAVIOUR OF L-80 CARBON STEEL IN SEA WATER

Picture for 02209 CAVITATION CORROSION BEHAVIOUR OF L-80...
Available for download
Product Number: 51300-02209-SG
ISBN: 02209 2002 CP
Author: A. AI-Hashem, J. Carew, W.Riad, and A.Abdullah
$0.00
$20.00
$20.00
Cavitation corrosion studies were conducted on L-80 carbon steel in seawater. The work included rate of mass loss versus time, potential time measurements in the presence and absence of cavitation tests which were conducted at a frequency of 20 kHz and 25°C. The rate of mass loss with time increased initially and then reached a steady state value after 50 h of cavitation. The corrosion potential shifted to less negative values after imposing cavitation conditions on this alloy. Cavitation attack on the surface of the alloy was revealed (by the SEM) in the form of cavity pits. It is believed that both mechanical and electro-chemical factors have lead to metal loss. Keywords: Cavity pit, cavitation, carbon steel, electrochemical seawater.
Cavitation corrosion studies were conducted on L-80 carbon steel in seawater. The work included rate of mass loss versus time, potential time measurements in the presence and absence of cavitation tests which were conducted at a frequency of 20 kHz and 25°C. The rate of mass loss with time increased initially and then reached a steady state value after 50 h of cavitation. The corrosion potential shifted to less negative values after imposing cavitation conditions on this alloy. Cavitation attack on the surface of the alloy was revealed (by the SEM) in the form of cavity pits. It is believed that both mechanical and electro-chemical factors have lead to metal loss. Keywords: Cavity pit, cavitation, carbon steel, electrochemical seawater.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 07253 Cavitation Corrosion Behavior of Carbon Steel, Al-Bronze and Cobalt-Based Alloy in Seawater
Available for download

07253 Cavitation Corrosion Behavior of Carbon Steel, Al-Bronze and Cobalt-Based Alloy in Seawater

Product Number: 51300-07253-SG
ISBN: 07253 2007 CP
Author: AbdulHameed Al-Hashem, H. Tarish, Ahmad A. Akbar
Publication Date: 2007
$20.00
Picture for 00637 THE EFFECT OF ULTRASONICALLY INDUCED
Available for download

00637 THE EFFECT OF ULTRASONICALLY INDUCED CAVITATION CONDITIONS ON THE BEHAVIOUR OF L-80 CARBON STEEL IN SEAWATER

Product Number: 51300-00637-SG
ISBN: 00637 2000 CP
Author: A. AI-Hashem, J. Carew and A. Abdullah
$20.00
Picture for 08173 Cavitation and Erosion Damage of Reboiler Stripper Tubes in Gas Manufacturing Industry
Available for download

08173 Cavitation and Erosion Damage of Reboiler Stripper Tubes in Gas Manufacturing Industry

Product Number: 51300-08173-SG
ISBN: 08173 2008 CP
Author: Hussein Rahmatalla, Mohammed Maqbool Ahmed, and Abdulla Radi Al-Hajri
Publication Date: 2008
$20.00

Two successive leakages were reported in the heat exchanger composed of 8 rows of finned tubes of the convection section of the condensate stripper re-boiler.  A comprehensive study (Failure Analysis) has been conducted to reveal the form of failure. The failure was recognized as erosion and cavitation damage.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support