Server maintenance is scheduled for Saturday, December 21st between 6am-10am CST.

During that time, parts of our website will be affected until maintenance is completed. Thank you for your patience.

Menu
Search
Filters
Close
Menu

Use GIVING24 at checkout to save 20% on eCourses and books (some exclusions apply)!

01496 STRESS CORROSION CRACKING OF STAINLESS STEEL COMPONENTS IN STEAM SERVICE

Picture for 01496 STRESS CORROSION CRACKING OF STAINLESS STEEL
Available for download
Product Number: 51300-01496-SG
ISBN: 01496 2001 CP
Author: Mel J.Esmacher
$0.00
$20.00
$20.00
The paper discusses stress corrosion cracking (SCC) of stainless steel components due to the ingress of caustic into steam systems. Also reviewed are case histories in which laboratory investigations assisted in identifying the root causes involved and proper corrective actions to resolve this problem. Keywords: caustic, steam, stress corrosion cracking, superheater, stainless steel.
The paper discusses stress corrosion cracking (SCC) of stainless steel components due to the ingress of caustic into steam systems. Also reviewed are case histories in which laboratory investigations assisted in identifying the root causes involved and proper corrective actions to resolve this problem. Keywords: caustic, steam, stress corrosion cracking, superheater, stainless steel.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03518 STRESS CORROSION CRACKING OF 304L
Available for download

03518 STRESS CORROSION CRACKING OF 304L STAINLESS STEEL IN SODIUM SULFIDE-CONTAINING CAUSTIC SOLUTIONS

Product Number: 51300-03518-SG
ISBN: 03518 2003 CP
Author: Preet M. Singh, Oluwatosin Ige, Jamshad Mahmood
Publication Date: 2003
$20.00

Austenitic stainless steels are susceptible to caustic stress corrosion cracking (SCC) above 121°C.  When sulfides are present in caustic solutions the SCC has been reported to occur at lower temperatures. This paper discusses a study of the role of sulfide in caustic solutions on SCC of austenitic stainless at T=~50°C.
Picture for 00596 STRESS CORROSION CRACKING OF STAINLESS
Available for download

00596 STRESS CORROSION CRACKING OF STAINLESS ALLOYS IN OXYGENATED CAUSTIC ENVIRONMENTS

Product Number: 51300-00596-SG
ISBN: 00596 2000 CP
Author: Stephen Clarke
$20.00
Picture for 98718 CONDENSATE CORROSION IN STEAM
Available for download

98718 CONDENSATE CORROSION IN STEAM GENERATING SYSTEMS

Product Number: 51300-98718-SG
ISBN: 98718 1998 CP
Author: Tzu-Yu Chen, Carol B. Batton, Daniel M. Cicero, Robert D. Port
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support