01389 LOCAL HEAVY CARBURIZATION OF OLEFIN PYROLYSIS FURNACE TUBE

Picture for 01389 LOCAL HEAVY CARBURIZATION OF
Available for download
Product Number: 51300-01389-SG
ISBN: 01389 2001 CP
Author: A. Kh. Bairamov and R. Bradley
$0.00
$20.00
$20.00
The results of this investigation, which revealed heavy carburization in a 25Cr/35Ni/1.5Nb olefin pyrolysis furnace tube being operated at about 850°(2 for approximately one year, are discussed. Severe localized damage was in the shape of isolated rounded cavities with diameters of 6-8 mm and depth of about 2 mm. Optical microscopy and SEM/EDX analysis of the areas under the pits showed secondary carbide precipitation at the grain boundaries and within the grains along with heavy intergranular attack up to complete separation of grains. The presence of three phases enriched by Cr or Nb along with chromium depleted regions adjacent to the grain boundaries were also revealed. Microhardness tests revealed hardnesses, which were 70-90% higher in the heavily carburized regions (exactly under the pits) than in the other unaffected regions. The results of the examination made it possible to conclude that the furnace tube failed due to a phenomenon known as metal dusting caused by the local deposition of"green oil" on the tube surface at the inlet of the furnace. Keywords: Olefin pyrolysis, green oil, furnace tube, secondary carbide, metal dusting, microhardness.
The results of this investigation, which revealed heavy carburization in a 25Cr/35Ni/1.5Nb olefin pyrolysis furnace tube being operated at about 850°(2 for approximately one year, are discussed. Severe localized damage was in the shape of isolated rounded cavities with diameters of 6-8 mm and depth of about 2 mm. Optical microscopy and SEM/EDX analysis of the areas under the pits showed secondary carbide precipitation at the grain boundaries and within the grains along with heavy intergranular attack up to complete separation of grains. The presence of three phases enriched by Cr or Nb along with chromium depleted regions adjacent to the grain boundaries were also revealed. Microhardness tests revealed hardnesses, which were 70-90% higher in the heavily carburized regions (exactly under the pits) than in the other unaffected regions. The results of the examination made it possible to conclude that the furnace tube failed due to a phenomenon known as metal dusting caused by the local deposition of"green oil" on the tube surface at the inlet of the furnace. Keywords: Olefin pyrolysis, green oil, furnace tube, secondary carbide, metal dusting, microhardness.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 01388 Effect of ID Surface Modification
Available for download

01388 Effect of ID Surface Modification on Carburization of Ethylene Furnace Tubes

Product Number: 51300-01388-SG
ISBN: 01388 2001 CP
Author: Arun R. Kurlekar, George T. Bayer, Gerald E. Gapinski
$20.00
Picture for 02386 A NEW CARBURIZATION RESISTANT ALLOY...
Available for download

02386 A NEW CARBURIZATION RESISTANT ALLOY FOR ETHYLENE PYROLYSIS FURNACE TUBES

Product Number: 51300-02386-SG
ISBN: 02386 2002 CP
Author: Y.Nishiyama, H.Semba, K.Ogawa, Y.Yamadera, Y.Sawaragi, and S.Kinomura
Publication Date: 2002
$20.00

A new wrought alloy has been developed for use as furnace tubes in ethylene pyrolysis plants. This alloy has an excellent carburization resistance due to uniform formation of protective Al2O3 oxide scale on the metal surface. Laboratory corrosion tests have been carried out to evaluate carburization resistance of the developed alloy.
Picture for 01392 A LOW COKING AND CARBURIZATION
Available for download

01392 A LOW COKING AND CARBURIZATION RESISTANT COATING FOR ETHYLENE PYROLYSIS FURNACES

Product Number: 51300-01392-SG
ISBN: 01392 2001 CP
Author: Ted Redmond, Dr. Yan Chen, Arthur Bailey, John Page
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support