01125 LONG-TERM DISSOLUTION BEHAVIOR OF ALLOY 22: EXPERIMENTS AND MODELING

Picture for 01125 LONG-TERM DISSOLUTION BEHAVIOR OF
Available for download
Product Number: 51300-01125-SG
ISBN: 01125 2001 CP
Author: D.S. Duma, C.S. Brossia, O. Pensado
$0.00
$20.00
$20.00
The long-term integrity of containers for the disposal of high-level nuclear waste in the absence of environmental conditions leading to localized corrosion and stress corrosion cracking is based on the assumption that passive dissolution of Alloy 22 is the dominant mechanism. Corrosion rate measurements under passive and transpassive conditions were performed as a function of temperature, solution pH, and chloride concentration. Analyses of solutions using capillary electrophoresis and the corrosion product deposit using SEM-EDS were performed in order to determine if dissolution was stoichiometric or if preferential dissolution of certain alloying elements was favored. Preliminary measurements suggest that under passive conditions, the dissolution rate is low and stoichiometric. Modeling of passive film dissolution also suggests that while preferential dissolution can occur in the short term, long-term dissolution is likely to be stoichiometric.

Keywords: Alloy 22, High level waste, passive corrosion, passive film chemistry, capillary electrophoresis
The long-term integrity of containers for the disposal of high-level nuclear waste in the absence of environmental conditions leading to localized corrosion and stress corrosion cracking is based on the assumption that passive dissolution of Alloy 22 is the dominant mechanism. Corrosion rate measurements under passive and transpassive conditions were performed as a function of temperature, solution pH, and chloride concentration. Analyses of solutions using capillary electrophoresis and the corrosion product deposit using SEM-EDS were performed in order to determine if dissolution was stoichiometric or if preferential dissolution of certain alloying elements was favored. Preliminary measurements suggest that under passive conditions, the dissolution rate is low and stoichiometric. Modeling of passive film dissolution also suggests that while preferential dissolution can occur in the short term, long-term dissolution is likely to be stoichiometric.

Keywords: Alloy 22, High level waste, passive corrosion, passive film chemistry, capillary electrophoresis
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 01132 LOCALIZED CORROSION OF ZIRCALOY
Available for download

01132 LOCALIZED CORROSION OF ZIRCALOY CLADDING UNDER REPOSITORY CONDITIONS

Product Number: 51300-01132-SG
ISBN: 01132 2001 CP
Author: M. G. Bale , V. Pasupathi , and Te-Lin Yau
$20.00
Picture for 01127 Effect of Palladium on the Localized
Available for download

01127 Effect of Palladium on the Localized and Passive Dissolution of Titanium

Product Number: 51300-01127-SG
ISBN: 01127 2001 CP
Author: C.S. Brossia and G.A. Cragnolino
$20.00
Picture for 01117 THE INFLUENCE OF DISSOLVED HYDROGEN
Available for download

01117 THE INFLUENCE OF DISSOLVED HYDROGEN ON NICKEL ALLOY SCC: A WINDOW TO FUNDAMENTAL INSIGHT

Product Number: 51300-01117-SG
ISBN: 01117 2001 CP
Author: D.S. Morton, S.A. Attanasio, G.A. Young, EL. Andresen, T.M. Angeliu
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support