01117 THE INFLUENCE OF DISSOLVED HYDROGEN ON NICKEL ALLOY SCC: A WINDOW TO FUNDAMENTAL INSIGHT

Picture for 01117 THE INFLUENCE OF DISSOLVED HYDROGEN
Available for download
Product Number: 51300-01117-SG
ISBN: 01117 2001 CP
Author: D.S. Morton, S.A. Attanasio, G.A. Young, EL. Andresen, T.M. Angeliu
$0.00
$20.00
$20.00
Prior stress corrosion crack growth rate (SCCGR) testing of nickel alloys as a function of the aqueous hydrogen concentration (i.e., the concentration of hydrogen dissolved in the water) has identified different functionalities at 338 and 360°C. These SCCGR dependencies have been uniquely explained in terms of the stability of nickel oxide. The present work evaluates whether the influence of aqueous hydrogen concentration on SCCGR is fundamentally due to effects on hydrogen absorption and/or corrosion kinetics. Hydrogen permeation tests were conducted to measure hydrogen pickup in and transport through the metal. Repassivation tests were performed in an attempt to quantify the corrosion kinetics. The aqueous hydrogen concentration dependency of these fundamental parameters (hydrogen permeation, repassivation) has been used to qualitatively evaluate the film-rupture/oxidation (FRO) and hydrogen assisted cracking (HAC) SCC mechanisms. This paper discusses the conditions that must be imposed upon these mechanisms to describe the known nickel alloy SCCGR aqueous hydrogen concentration functionality. Specifically, the buildup of hydrogen witl'/in Alloy 600 (measured through permeability) does not exhibit the same functionality as SCC with respect to the aqueous hydrogen concentration. This result implies that if HAC is the dominant SCC mechanism, then corrosion at isolated active path regions (i.e., surface initiation sites or cracks) must be the source of localized elevated detrimental hydrogen. Repassivation tests showed little temperature sensitivity over the range of 204 to 360°C. This result implies that for either the FRO or the HAC mechanism, corrosion processes (e.g., at a crack tip, in the crack wake, or on surfaces external to the crack) cannot by themselves explain the strong temperature dependence of nickel alloy SCC. Keywords: SCC, hydrogen, nickel alloys, permeation, repassivation, corrosion
Prior stress corrosion crack growth rate (SCCGR) testing of nickel alloys as a function of the aqueous hydrogen concentration (i.e., the concentration of hydrogen dissolved in the water) has identified different functionalities at 338 and 360°C. These SCCGR dependencies have been uniquely explained in terms of the stability of nickel oxide. The present work evaluates whether the influence of aqueous hydrogen concentration on SCCGR is fundamentally due to effects on hydrogen absorption and/or corrosion kinetics. Hydrogen permeation tests were conducted to measure hydrogen pickup in and transport through the metal. Repassivation tests were performed in an attempt to quantify the corrosion kinetics. The aqueous hydrogen concentration dependency of these fundamental parameters (hydrogen permeation, repassivation) has been used to qualitatively evaluate the film-rupture/oxidation (FRO) and hydrogen assisted cracking (HAC) SCC mechanisms. This paper discusses the conditions that must be imposed upon these mechanisms to describe the known nickel alloy SCCGR aqueous hydrogen concentration functionality. Specifically, the buildup of hydrogen witl'/in Alloy 600 (measured through permeability) does not exhibit the same functionality as SCC with respect to the aqueous hydrogen concentration. This result implies that if HAC is the dominant SCC mechanism, then corrosion at isolated active path regions (i.e., surface initiation sites or cracks) must be the source of localized elevated detrimental hydrogen. Repassivation tests showed little temperature sensitivity over the range of 204 to 360°C. This result implies that for either the FRO or the HAC mechanism, corrosion processes (e.g., at a crack tip, in the crack wake, or on surfaces external to the crack) cannot by themselves explain the strong temperature dependence of nickel alloy SCC. Keywords: SCC, hydrogen, nickel alloys, permeation, repassivation, corrosion
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03675 The Effect of pH on Nickel Alloy SCC and
Available for download

03675 The Effect of pH on Nickel Alloy SCC and Corrosion Performance

Product Number: 51300-03675-SG
ISBN: 03675 2003 CP
Author: D.S. Morton, and M Hansen
$20.00
Picture for 07421 Fabricating Nickel Alloy Products to Avoid Stress Relaxation Cracking
Available for download

07421 Fabricating Nickel Alloy Products to Avoid Stress Relaxation Cracking

Product Number: 51300-07421-SG
ISBN: 07421 2007 CP
Author: Lewis E. Shoemaker, Gaylord D. Smith, Brian A. Baker, and Jon Poole
Publication Date: 2007
$20.00

Various alloys subjected various heat treatments were examined in-service and tested to determine their susceptibility to stress relaxation cracking.
Picture for 99447 INFLUENCE OF DISSOLVED HYDROGEN ON
Available for download

99447 INFLUENCE OF DISSOLVED HYDROGEN ON NICKEL ALLOY SCC IN HIGH TEMPERATURE WATER

Product Number: 51300-99447-SG
ISBN: 99447 1999 CP
Author: D.S. Morton, S.A. Attanasio, J.S. Fish and M.K. Schurman
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support