00700 FAILURE OF POLYPROPYLENE LINED PIPE IN SULFURIC ACID - A CASE HISTORY

Picture for 00700 FAILURE OF POLYPROPYLENE LINED PIPE IN
Available for download
Product Number: 51300-00700-SG
ISBN: 00700 2000 CP
Author: Ali A. A1-Beed
$0.00
$20.00
$20.00
Polypropylene (PP) and PVDF lined pipe experienced frequent failures in spent (60-78%) sulfuric acid after about seven to ten years in service. The failures were due to exceeding the design temperature when mixing 98% acid where high temperature is generated which then created thermal stress in the liner and bolted flared joints and developed cracks and product leaks. The PP was replaced by Polytetrafluoroethylene (PTFE) lined pipe using proper bolting torque. PTFE has been in service for more than 7 years without any failure Key words: Polypropylene, Polytetrafluoroethylene, Spent Sulfuric acid, Polyvinylidene Chloride.
Polypropylene (PP) and PVDF lined pipe experienced frequent failures in spent (60-78%) sulfuric acid after about seven to ten years in service. The failures were due to exceeding the design temperature when mixing 98% acid where high temperature is generated which then created thermal stress in the liner and bolted flared joints and developed cracks and product leaks. The PP was replaced by Polytetrafluoroethylene (PTFE) lined pipe using proper bolting torque. PTFE has been in service for more than 7 years without any failure Key words: Polypropylene, Polytetrafluoroethylene, Spent Sulfuric acid, Polyvinylidene Chloride.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 01342 Metallic Materials for Concentrated Sulfuric
Available for download

01342 Metallic Materials for Concentrated Sulfuric Acid Service

Product Number: 51300-01342-SG
ISBN: 01342 2001 CP
Author: Michael H. W. Renner
$20.00
Picture for 06225 A PRACTICAL GUIDE TO USE OF NICKEL ALLOYS
Available for download

06225 A PRACTICAL GUIDE TO USE OF NICKEL ALLOYS FOR SULFURIC ACID SERVICE

Product Number: 51300-06225-SG
ISBN: 06225 2006 CP
Author: Edward L. Hibner, Lewis E. Shoemaker
$20.00
Picture for 04233 Alloy Selection for Dilute and Medium
Available for download

04233 Alloy Selection for Dilute and Medium Concentration Sulfuric Acid

Product Number: 51300-04233-SG
ISBN: 04233 2004 CP
Author: Ulrich Brill and Helena Alves, ThyssenKrupp VDM GmbH
Publication Date: 2004
$20.00

Sulfuric acid is one of the most important elementary substances of the chemical industry.  There is no stainless steel or even a nickel base alloy available which is suitable over the entire concentration range.  This paper will give corrosion data in up to 75 % sulfuric acid at boiling temperature for various commercial grades as well as for some new developmental alloys.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support