00163 CORROSIVITY OF METHANOLIC SYSTEMS IN WET SOUR GAS PRODUCTION

Picture for 00163 CORROSIVITY OF METHANOLIC SYSTEMS IN
Available for download
Product Number: 51300-00163-SG
ISBN: 00163 2000 CP
Author: G. Siegmund, G. Schmitt, B. Sadlowsky
$0.00
$20.00
$20.00
During start-up of sour gas wells methanol is added in order to prevent hydrate formation in the piping. Earlier own results and literature data showed, that SSC is likely to occur at carbon steel if methanol is present in sour wet media. Therefore, the SSC risk of pipeline steel in methanol and aqueous methanolic solutions was tested with tensile probes under 16 bar H2S and 16 bar H2S + 8 bar CO2. In the absence of corrosion inhibitors the steel suffered severe SSC which, however, could be prevented with selected corrosion inhibitors. The oxgen contained in the technical grade methanol used in the experiment, but also in the service, increases the corrosion severity of the methanolic systems significantly. Keywords: methanol, wet sour gas, hydrogen sulphide, carbon steel, linepipe steel, hydrogen, sulphide stress cracking, SSC, SOHIC, inhibitors
During start-up of sour gas wells methanol is added in order to prevent hydrate formation in the piping. Earlier own results and literature data showed, that SSC is likely to occur at carbon steel if methanol is present in sour wet media. Therefore, the SSC risk of pipeline steel in methanol and aqueous methanolic solutions was tested with tensile probes under 16 bar H2S and 16 bar H2S + 8 bar CO2. In the absence of corrosion inhibitors the steel suffered severe SSC which, however, could be prevented with selected corrosion inhibitors. The oxgen contained in the technical grade methanol used in the experiment, but also in the service, increases the corrosion severity of the methanolic systems significantly. Keywords: methanol, wet sour gas, hydrogen sulphide, carbon steel, linepipe steel, hydrogen, sulphide stress cracking, SSC, SOHIC, inhibitors
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 07663 The Effect of Oxygenated Methanol on Corrosion in Sour Wet Gas Environments
Available for download

07663 The Effect of Oxygenated Methanol on Corrosion in Sour Wet Gas Environments

Product Number: 51300-07663-SG
ISBN: 07663 2007 CP
Author: Neil Park, Sherif Maksoud, Lara Morello, and Jennifer E. Wong
Publication Date: 2007
$20.00

This paper studies the effect of oxygen in methanol on the structures and growth kinetics of iron sulfide scales. Gravimetric weight analysis was used to evaluate the corrosion mechanisms and rates. Scanning Electron Microscope/ Energy Dispersive X-ray Spectrometry (SEM/EDX), Optical Microscope and X-ray Diffraction (XRD) were used to analyze the scale.

 
Picture for Methanol-Induced Internal Stress Corrosion Cracking in a Northern Petroleum Pipeline
Available for download

51314-3985-Methanol-Induced Internal Stress Corrosion Cracking in a Northern Petroleum Pipeline

Product Number: 51314-3985-SG
ISBN: 3985 2014 CP
Author: Barbara Padgett
Publication Date: 2014
$20.00
Picture for 97493 Materials Experience in Methanol Reforming
Available for download

97493 Materials Experience in Methanol Reforming Units

Product Number: 51300-97493-SG
ISBN: 97493 1997 CP
Author: K. L. Baumert, J. J. Hoffman
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support