Available for download

51316-7126-Qualification of Super 13Cr-110 in HPHT Sour Well Service with Concentrated Brines

Product Number: 51316-7126-SG

ISBN: 7126 2016 CP

Author: Fengmei Song

Publication Date: 2016

$20.00

A corrosion cracking assessment evaluated a 13Cr-5Ni-2Mo 110 ksi grade martensitic stainless steel as a potential well tubing material for oil and gas production from Gulf of Mexico reservoirs. Also, Stress Corrosion Cracking at low H2S/low temp/high acidity (pH<3.5) was tested by Cyclic Slow Strain Rate.

Available for download

NACE TM0177-2005, Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments

Product Number: NACE TM0177-2005

Publication Date: 2005

$179.00

HISTORICAL DOCUMENT.

This standard addresses the testing of metals for resistance to cracking failure under the combined action of tensile stress and corrosion in aqueous environments containing hydrogen sulfide (H2S). This phenomenon is generally termed sulfide stress cracking (SSC) when operating at room temperature and stress corrosion cracking (SCC) when operating at higher temperatures. In recognition of the variation with temperature and with different materials this phenomenon is herein called environmental cracking (EC). For the purposes of this standard, EC includes only SSC, SCC, and hydrogen stress cracking (HSC).

Products tagged with 'c-ring test'

51316-7126-Qualification of Super 13Cr-110 in HPHT Sour Well Service with Concentrated Brines

NACE TM0177-2005, Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments