51316-7669-Performance of Thermally Sprayed CRA Coatings on Carbon Steel in Supercritical CO2 Environments

Picture for Performance of Thermally Sprayed CRA Coatings on Carbon Steel in Supercritical CO2 Environments
Available for download
Product Number: 51316-7669-SG
ISBN: 7669 2016 CP
Author: Shiladitya Paul
Publication Date: 2016
$0.00
$20.00
$20.00
This paper reports the use of a thermal spray corrosion resistant alloy (CRA) coatings to mitigate corrosion of carbon steel in an environment containing high pressure supercritical CO2 and an aqueous phase. CRA coatings were sprayed using high velocity oxy-fuel (HVOF) onto carbon steel substrates holidays were drilled in one set of specimens to expose the steel substrate and tested in 3.5wt.% NaCl solution at 40°C and 80°C for 30days bubbled with 10MPa CO2. Microstructural characterization revealed that the undamaged coatings protected the steel substrate from CO2 corrosion. The bare steel formed a siderite scale while no such scale was seen in the case of CRA-coated steel. The CRA coatings with holidays showed corrosion of the carbon steel substrate. The substrate close to the coating showed accelerated corrosion due to galvanic effects.It can be concluded that thermally sprayed CRA coatings can provide a cost-effective corrosion mitigation method for infrastructure likely to be in contact with wet supercritical CO2. The same coatings can be used as inner lining of pipes for transport of impure CO2. However care must be taken to ensure that the thermally sprayed layer does not have any through porosity; else such coatings may accelerate corrosion of the underlying steel due to galvanic interactions.
This paper reports the use of a thermal spray corrosion resistant alloy (CRA) coatings to mitigate corrosion of carbon steel in an environment containing high pressure supercritical CO2 and an aqueous phase. CRA coatings were sprayed using high velocity oxy-fuel (HVOF) onto carbon steel substrates holidays were drilled in one set of specimens to expose the steel substrate and tested in 3.5wt.% NaCl solution at 40°C and 80°C for 30days bubbled with 10MPa CO2. Microstructural characterization revealed that the undamaged coatings protected the steel substrate from CO2 corrosion. The bare steel formed a siderite scale while no such scale was seen in the case of CRA-coated steel. The CRA coatings with holidays showed corrosion of the carbon steel substrate. The substrate close to the coating showed accelerated corrosion due to galvanic effects.It can be concluded that thermally sprayed CRA coatings can provide a cost-effective corrosion mitigation method for infrastructure likely to be in contact with wet supercritical CO2. The same coatings can be used as inner lining of pipes for transport of impure CO2. However care must be taken to ensure that the thermally sprayed layer does not have any through porosity; else such coatings may accelerate corrosion of the underlying steel due to galvanic interactions.
Product tags
Also Purchased
Picture for Performance of Thermally Sprayed Corrosion Resistant Alloy (CRA) Coatings in 50MPa Supercritical CO2
Available for download

Performance of Thermally Sprayed Corrosion Resistant Alloy (CRA) Coatings in 50MPa Supercritical CO2

Product Number: 51317--9007-SG
ISBN: 9007 2017 CP
Author: Shiladitya Paul
Publication Date: 2017
$20.00

This paper reports the performance of HVOF-sprayed corrosion resistant alloy (CRA) coatings in an aqueous solution bubbled with 50MPa supercritical CO2.

Picture for 08430 Corrosion of Materials in Supercritical CO2 Environments
Available for download

08430 Corrosion of Materials in Supercritical CO2 Environments

Product Number: 51300-08430-SG
ISBN: 08430 2008 CP
Author: R. Ballinger, J. Lim, T. McKrell, and G. Eastwick
Publication Date: 2008
$20.00
Picture for Tank Linings Cure Response during Cold Winter Months; Ready for Immersion Service?
Available for download

51316-7668-Tank Linings Cure Response during Cold Winter Months; Ready for Immersion Service?

Product Number: 51316-7668-SG
ISBN: 7668 2016 CP
Author: Nicole Mackey
Publication Date: 2016
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support