51315-6132-Evaluation of Atmospheric Chloride-Induced Stress Corrosion Cracking of Stainless Steel Canister

Product Number: 51315-6132-SG
ISBN: 6132 2015 CP
Author: Hundal Jung
Publication Date: 2015
$0.00
$20.00
$20.00
Most canisters for spent fuel dry storage in the US are fabricated from austenitic stainless steel. When exposed to chloride containing atmosphere in marine environment welded canister can be susceptible to chloride-induced stress corrosion cracking that can affect confinement function as a result of crack initiation and propagation through canister wall thickness.In assessment key factors affecting CISCC are identified in terms of environments (temperature relative humidity and chloride concentration) stresses and material conditions. A methodology to estimate the time for crack initiation and crack penetration depth as a function of time is proposed and technical gaps are discussed. An evaluation of operation experience for the outer diameter SCC of stainless steel piping at power plants are also performed for comparison
Most canisters for spent fuel dry storage in the US are fabricated from austenitic stainless steel. When exposed to chloride containing atmosphere in marine environment welded canister can be susceptible to chloride-induced stress corrosion cracking that can affect confinement function as a result of crack initiation and propagation through canister wall thickness.In assessment key factors affecting CISCC are identified in terms of environments (temperature relative humidity and chloride concentration) stresses and material conditions. A methodology to estimate the time for crack initiation and crack penetration depth as a function of time is proposed and technical gaps are discussed. An evaluation of operation experience for the outer diameter SCC of stainless steel piping at power plants are also performed for comparison
Also Purchased
Picture for 09295 Atmospheric Chamber Testing to Evalute Chloride Induced Stress Corrosion Cracking of Type 304,
Available for download

09295 Atmospheric Chamber Testing to Evalute Chloride Induced Stress Corrosion Cracking of Type 304, 304L, and 316L Stainless Steel

Product Number: 51300-09295-SG
ISBN: 09295 2009 CP
Author: Darrell Dunn and Todd S. Mintz
Publication Date: 2009
$20.00
Picture for 08484 Low Temperature Stress Corrosion Cracking of Stainless Steels in the Atmosphere in Presence of
Available for download

08484 Low Temperature Stress Corrosion Cracking of Stainless Steels in the Atmosphere in Presence of Chloride Deposits

Product Number: 51300-08484-SG
ISBN: 08484 2008 CP
Author: Tomas Prosek, Anna Iversen, and Claes Taxen
Publication Date: 2008
$20.00