51312-01705-A Study on the Effects of Cutting Fume for Coating Performance of Steel Plate

Picture for A Study on the Effects of Cutting Fume for Coating Performance of Steel Plate
Available for download
Product Number: 51312-01705-SG
ISBN: 01705 2012 CP
Author: Chung Seo Park
Publication Date: 2012
$0.00
$20.00
$20.00
Shop primer coated film is easily attached by the penetration of cutting fumes and the residual cutting fumes cannot be completely removed by blast cleaning in the ship yard. Therefore additional power tool cleaning is required to remove residual cutting fumes before coating application. In this study the establishment of the surface preparation criteria on the fume attached steel surface was performed by means of coating performance evaluation as the degree of the cutting fume attachment with 6 grades 100%(G1) to 0%(G6). From the test results even though the cutting fumes remain on the surface the coating does not lose its original adhesion property on the surface comparing to where cutting fumes not remain. All panels were good condition without the concentration rate fume according to sea water immersion test for 6 months and the higher residual rate of fume showed the better rust creep resistance from the salt spray test for 1000 and 2000hours.
Shop primer coated film is easily attached by the penetration of cutting fumes and the residual cutting fumes cannot be completely removed by blast cleaning in the ship yard. Therefore additional power tool cleaning is required to remove residual cutting fumes before coating application. In this study the establishment of the surface preparation criteria on the fume attached steel surface was performed by means of coating performance evaluation as the degree of the cutting fume attachment with 6 grades 100%(G1) to 0%(G6). From the test results even though the cutting fumes remain on the surface the coating does not lose its original adhesion property on the surface comparing to where cutting fumes not remain. All panels were good condition without the concentration rate fume according to sea water immersion test for 6 months and the higher residual rate of fume showed the better rust creep resistance from the salt spray test for 1000 and 2000hours.
Product tags
Also Purchased
Picture for A Method to Determine the Internal Current Effect on Corrosion Rate Measurements with Coupled Multie
Available for download

51312-01707-A Method to Determine the Internal Current Effect on Corrosion Rate Measurements with Coupled Multie

Product Number: 51312-01707-SG
ISBN: 01707 2012 CP
Author: Xiaodong Sun
Publication Date: 2012
$20.00
Picture for Pitting resistance evaluation of stainless steel 316L in presence of neat production chemicals by us
Available for download

51312-01703-Pitting resistance evaluation of stainless steel 316L in presence of neat production chemicals by us

Product Number: 51312-01703-SG
ISBN: 01703 2012 CP
Author: Yolanda De-Abreu
Publication Date: 2012
$20.00
Picture for Development of Cost-effective Ni Alloy OCTG material for Sour Environment
Available for download

51312-01684-Development of Cost-effective Ni Alloy OCTG material for Sour Environment

Product Number: 51312-01684-SG
ISBN: 01684 2012 CP
Author: Masayuki Sagara
Publication Date: 2012
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support