99065 Variables Affecting Mixed Oxidant Corrosion of Stainless Steels in Gasifiers

Picture for 99065 Variables Affecting Mixed Oxidant Corrosion
Available for download
Product Number: 51300-99065-SG
ISBN: 99065 1999 CP
Author: Wate T. Bakker
$0.00
$20.00
$20.00
This paper is the final installment of EPRI’s project on corrosion in syngas coolers of integrated coal gasification combined cycle plant. In previous papers we explored the effect of chloride species on mixed oxidant corrosion of stainless steels (Corrosion 97, Paper 134) and iron aluminizes (Corrosion 98, Paper 185). It was found that the amount of chloride species in the gas and in deposits largely determined the rate of corrosion. Armed with this understanding the effect of a few common process variables is explored in this paper. It was found that corrosion rates decline at higher temperatures, when chloride-enhanced mixed oxidant corrosion occurs at lower temperatures, but corrosion rates increase with temperature for pure sulfidation/oxidation, as maybe expected. System pressure was generally of secondary importance, but again higher corrosion rates were generally experienced at elevated pressure, when chloride-enhanced corrosion was predominant, especially at lower temperatures. A simulated temperature excursion below the syngas dewpoint had similar effects, and also caused chloride-enhanced corrosion in 310 stainless steel, which usually does not show this type of corrosion, except when exposed to aqueous corrosion during downtime. A pleasant surprise was the almost complete lack of corrosion when H2S and HCl levels were reduced to those expected downstream from gasifiers using in-bed desulfurization. It would appear that 12Cr steels may be adequate here. This is being explored further.
This paper is the final installment of EPRI’s project on corrosion in syngas coolers of integrated coal gasification combined cycle plant. In previous papers we explored the effect of chloride species on mixed oxidant corrosion of stainless steels (Corrosion 97, Paper 134) and iron aluminizes (Corrosion 98, Paper 185). It was found that the amount of chloride species in the gas and in deposits largely determined the rate of corrosion. Armed with this understanding the effect of a few common process variables is explored in this paper. It was found that corrosion rates decline at higher temperatures, when chloride-enhanced mixed oxidant corrosion occurs at lower temperatures, but corrosion rates increase with temperature for pure sulfidation/oxidation, as maybe expected. System pressure was generally of secondary importance, but again higher corrosion rates were generally experienced at elevated pressure, when chloride-enhanced corrosion was predominant, especially at lower temperatures. A simulated temperature excursion below the syngas dewpoint had similar effects, and also caused chloride-enhanced corrosion in 310 stainless steel, which usually does not show this type of corrosion, except when exposed to aqueous corrosion during downtime. A pleasant surprise was the almost complete lack of corrosion when H2S and HCl levels were reduced to those expected downstream from gasifiers using in-bed desulfurization. It would appear that 12Cr steels may be adequate here. This is being explored further.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99067 HOT CORROSION BURNER RIG TESTING OF
Available for download

99067 HOT CORROSION BURNER RIG TESTING OF VARIOUS COMMERCIAL ALLOYS

Product Number: 51300-99067-SG
ISBN: 99067 1999 CP
Author: C. Regan, M. A. Harper and J. E. Barnes
$20.00
Picture for 99066 EFFECT OF LOW SULFUR CONTENTS IN A SIMULATED
Available for download

99066 EFFECT OF LOW SULFUR CONTENTS IN A SIMULATED SUB-STOICHIOMETRIC REHEAT FURNACE ENVIRONMENT ON THE OXIDATION KINETICS OF CARBON STEELS

Product Number: 51300-99066-SG
ISBN: 99066 1999 CP
Author: H.J.V. Lee, D. J. Young, B. Gleeson
$20.00
Picture for 99069 CORROSION OF HEAT EXCHANGER ALLOYS
Available for download

99069 CORROSION OF HEAT EXCHANGER ALLOYS EXPOSED TO A NON-EQUILIBRATED CO-BASED SULFIDIZING ENVIRONMENT AT 550°C

Product Number: 51300-99069-SG
ISBN: 99069 1999 CP
Author: Wate T. Bakker, James F. Norton and Mark Maier
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support