07593 On the Anodic Polarization Behavior of Carbon Steel in Hanford Nuclear Wastes

Picture for 07593 On the Anodic Polarization Behavior of Carbon Steel in Hanford Nuclear Wastes
Available for download
Product Number: 51300-07593-SG
ISBN: 07593 2007 CP
Author: F. Gu, C. Brossia, J. Beavers, C. Mendez, G. Frankel, G. Edgemon, and H. Berman
Publication Date: 2007
$0.00
$20.00
$20.00
The effect of the important chemical constituents in the Handford nuclear waste simulant on the anodic behavior of carbon steel was studied. Specifically, the effect of pH, nitrite concentration, nitrite/nitrate concentration ratios, total organic carbon and the chloride concentration on the open circuit potential, pitting potential and repassivation potential was evaluated. It was found that pH adjusting, although capable of returning the tank chemistry back to specification, did not significantly reduce the corrosivity of the stimulant compared to the present condition. Nitrite was found to be a potent inhibitor for carbon steel. A critical concentration of approximately 1.2M appeared to be beneficial to increase the difference of repassivation potential and open circuit potential considerably and thus prevent pitting corrosion from occurring. No further benefit was gained when increasing nitrite concentration to a higher level. The organic compounds were found to be weak inhibitors in the absence of nitrite and the change of chloride from 0.05M to 0.2M did not alter the anodic behavior dramatically.
The effect of the important chemical constituents in the Handford nuclear waste simulant on the anodic behavior of carbon steel was studied. Specifically, the effect of pH, nitrite concentration, nitrite/nitrate concentration ratios, total organic carbon and the chloride concentration on the open circuit potential, pitting potential and repassivation potential was evaluated. It was found that pH adjusting, although capable of returning the tank chemistry back to specification, did not significantly reduce the corrosivity of the stimulant compared to the present condition. Nitrite was found to be a potent inhibitor for carbon steel. A critical concentration of approximately 1.2M appeared to be beneficial to increase the difference of repassivation potential and open circuit potential considerably and thus prevent pitting corrosion from occurring. No further benefit was gained when increasing nitrite concentration to a higher level. The organic compounds were found to be weak inhibitors in the absence of nitrite and the change of chloride from 0.05M to 0.2M did not alter the anodic behavior dramatically.
Product tags
Also Purchased
Picture for 07581 Environmental and Geometrical Conditions to Sustain Crevice in Alloy 22
Available for download

07581 Environmental and Geometrical Conditions to Sustain Crevice in Alloy 22

Product Number: 51300-07581-SG
ISBN: 07581 2007 CP
Author: Ricardo M. Carranza, Martin A. Rodriguez, and Raul B. Rebak
Publication Date: 2007
$20.00
Picture for 07577 Long-Term Electrochemical Behavior of Creviced and Non-Creviced Alloy 22 in CaCl2 + Ca(NO3)2 B
Available for download

07577 Long-Term Electrochemical Behavior of Creviced and Non-Creviced Alloy 22 in CaCl2 + Ca(NO3)2 Brines

Product Number: 51300-07577-SG
ISBN: 07577 2007 CP
Author: Raul B. Rebak, Martin A. Rodriguez, and Marshall L. Stuart
Publication Date: 2007
$20.00
Picture for 07579 The Electrochemical Behavior of Alloy 22 in Extreme Chloride and Nitrate Environments
Available for download

07579 The Electrochemical Behavior of Alloy 22 in Extreme Chloride and Nitrate Environments

Product Number: 51300-07579-SG
ISBN: 07579 2007 CP
Author: Gabriel O. Ilevbare, Steve R. Gordon, and Robert Etien
Publication Date: 2007
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support