03693 CORROSION BEHAVIOR OF ALLOY 22 UNDER CONDITIONS OF DYNAMIC GROUNDWATER COMPOSITION

Product Number: 51300-03693-SG
ISBN: 03693 2003 CP
Author: A.L. Pulvirenti, K.M. Needham, M.A. Adel-Hadadi, E.J. Bishop, A. Barkatt, C.R. Marks and J.A. Gorma
$0.00
$20.00
$20.00
Solutions that simulated the compositions of saturated (J 13) and unsaturated (UZ) waters that can be found in the vicinity of Yucca Mountain were distilled to near dryness. The pH of both the condensates and residual solutions of J 13-based waters rose during the distillations, while the pH of both the condensates and residual solutions of UZ-based water experienced a large drop in pH during distillation, which could be caused by precipitation and slow redissolution of magnesium oxide solids. Samples of Alloy 22 immersed in condensates and residual solutions of UZ distillations exhibited general corrosion at rates ranging from 30-600 gm/year, and one sample exhibited pitting. Samples tested in solutions of 1000xJ 13 in which the pH was altered during testing showed an increase in corrosion rate over solutions of constant pH.
Solutions that simulated the compositions of saturated (J 13) and unsaturated (UZ) waters that can be found in the vicinity of Yucca Mountain were distilled to near dryness. The pH of both the condensates and residual solutions of J 13-based waters rose during the distillations, while the pH of both the condensates and residual solutions of UZ-based water experienced a large drop in pH during distillation, which could be caused by precipitation and slow redissolution of magnesium oxide solids. Samples of Alloy 22 immersed in condensates and residual solutions of UZ distillations exhibited general corrosion at rates ranging from 30-600 gm/year, and one sample exhibited pitting. Samples tested in solutions of 1000xJ 13 in which the pH was altered during testing showed an increase in corrosion rate over solutions of constant pH.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03682 LOCALIZED CORROSION SUSCEPTIBILITY OF NICKEL
Available for download

03682 LOCALIZED CORROSION SUSCEPTIBILITY OF NICKEL ALLOYS IN HALIDE CONTAINING ENVIRONMENTS

Product Number: 51300-03682-SG
ISBN: 03682 2003 CP
Author: Nacéra S. Meck, Paul Crook, S. Daniel Day, Raúl B. Rebak
$20.00
Picture for 03687 ON APPARENT BI-LINEAR CORROSION RATE
Available for download

03687 ON APPARENT BI-LINEAR CORROSION RATE BEHAVIOR OF TI GRADE 7 IN BASIC SATURATED WATER (BSW-12) BELOW AND ABOVE 80°C

Product Number: 51300-03687-SG
ISBN: 03687 2003 CP
Author: Fred Hua, Gerald Gordon
$20.00
Picture for 03690 EFFECT OF MEASUREMENT METHODS AND SOLUTION
Available for download

03690 EFFECT OF MEASUREMENT METHODS AND SOLUTION CHEMISTRY ON THE EVALUATION OF THE LOCALIZED CORROSION OF CANDIDATE HIGH-LEVEL WASTE CONTAINER MATERIALS

Product Number: 51300-03690-SG
ISBN: 03690 2003 CP
Author: Vijay Jain, Darrell Dunn, Narasi Sridhar, and Lietai Yang
$20.00