03212 Corrosion Behavior of Anodized AZ91D Magnesium Alloy

Product Number: 51300-03212-SG
ISBN: 03212 2003 CP
Author: Houng-Yu Hsiao and Wen-Ta Tsai
$0.00
$20.00
$20.00
The effect of anodization on the corrosion behavior of die-casted AZ91D Mg alloy in aqueous solution was studied. Anodization was performed in 3 M KOH + 0.21 M Na3PO4 + 0.6 M KF base electrolyte, with and without Al(NO3)3 addition. The anodized film was characterized by using x-ray diffraction (XRD), scanning electron microscopy (SEM), and x-ray photoelectron spectroscopy (XPS). The corrosion resistance of the various anodized alloys was then evaluated in 3.5 wt% NaCl solution using electrochemical impedance spectroscopy (EIS). The results showed that the anodized film was mainly composed of MgO, and the film properties were dependent on the condition of anodization process. Electrochemical testing results showed that AZ91D Mg alloy exhibited satisfactory corrosion resistance when anodized in the base electrolyte with 0.15 M Al(NO3)3 addition. Keywords: AZ91D Mg alloy, anodization treatment, corrosion resistance
The effect of anodization on the corrosion behavior of die-casted AZ91D Mg alloy in aqueous solution was studied. Anodization was performed in 3 M KOH + 0.21 M Na3PO4 + 0.6 M KF base electrolyte, with and without Al(NO3)3 addition. The anodized film was characterized by using x-ray diffraction (XRD), scanning electron microscopy (SEM), and x-ray photoelectron spectroscopy (XPS). The corrosion resistance of the various anodized alloys was then evaluated in 3.5 wt% NaCl solution using electrochemical impedance spectroscopy (EIS). The results showed that the anodized film was mainly composed of MgO, and the film properties were dependent on the condition of anodization process. Electrochemical testing results showed that AZ91D Mg alloy exhibited satisfactory corrosion resistance when anodized in the base electrolyte with 0.15 M Al(NO3)3 addition. Keywords: AZ91D Mg alloy, anodization treatment, corrosion resistance
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03208 35 YEARS OF CORROSION PROTECTION AT THE
Available for download

03208 35 YEARS OF CORROSION PROTECTION AT THE KENNEDY SPACE CENTER

Product Number: 51300-03208-SG
ISBN: 03208 2003 CP
Author: Luz Marina Calle and Louis G. MacDowell
$20.00
Picture for 03192 A QUANTITATIVE PROBABALISTIC APPROACH
Available for download

03192 A QUANTITATIVE PROBABALISTIC APPROACH TO EXTERNAL CORROSION DIRECT ASSESSMENT USING STRUCTURAL RELIABILITY ANALYSIS

Product Number: 51300-03192-SG
ISBN: 03192 2003 CP
Author: Mark McQueen, Will Burks, Virgil Wallace and Ray Hicks
$20.00
Picture for 03211 ENVIRONMENTALLY ASSISTED CRACKING
Available for download

03211 ENVIRONMENTALLY ASSISTED CRACKING PROPERTIES OF AA7249 EXTRUSIONS FOR AEROSPACE APPLICATIONS

Product Number: 51300-03211-SG
ISBN: 03211 2003 CP
Author: Kristen L. Deffenbaugh, Michelle G. Koul and Angela L. Moran
$20.00