Material selection is very critical and crucial for sour systems. Following standards and regulations alone is not sufficient to prevent failures that may occur if account is not taken of other aspects of corrosion. This paper shows how UNS N07750, that NACE MR0175 lists as resistant to cracking in sour service, failed due to sensitization, a deficiency that MR0175 does not prevent. Keywords: hydrogen embrittlement, sour gas, UNS N07750, sensitization, nickel base alloy, material selection.
Material selection is very critical and crucial for sour systems. Following standards and regulations alone is not sufficient to prevent failures that may occur if account is not taken of other aspects of corrosion. This paper shows how UNS N07750, that NACE MR0175 lists as resistant to cracking in sour service, failed due to sensitization, a deficiency that MR0175 does not prevent. Keywords: hydrogen embrittlement, sour gas, UNS N07750, sensitization, nickel base alloy, material selection.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for Susceptibility to Hydrogen Induced Stress Cracking of Alloy 718 and Alloy 725 Under Cathodic Polarization
Available for download

Susceptibility to Hydrogen Induced Stress Cracking of Alloy 718 and Alloy 725 Under Cathodic Polarization

Product Number: 51315-5597-SG
ISBN: 5597 2015 CP
Author: Gaute Stenerud
Publication Date: 2015
$20.00

 A test project to examine the susceptibility of Hydrogen Induced Stress Cracking (HISC) has been executed. In this project hydrogen charged samples of Alloy 718 and Alloy 725 have been exposed under tensile stress to establish critical stress levels for initiation of HISC.
Picture for The Effect of Hydrogen on Plain and Notched Test Specimens of PH Nickel Alloys
Available for download

51317--9655-The Effect of Hydrogen on Plain and Notched Test Specimens of PH Nickel Alloys

Product Number: 51317--9655-SG
ISBN: 9655 2017 CP
Author: Stephen McCoy
Publication Date: 2017
$20.00

This paper reviews previous work and shows laboratory results using different test techniques to demonstrate the influence of yield strength and microstructure on the resistance to Hydrogen Stress Cracking of precipitation hardenable Nickel alloys N07718, N09925, N07725, N09945 and N09946.

Picture for 03129 OFFSHORE NICKEL ALLOY TUBING HANGER
Available for download

03129 OFFSHORE NICKEL ALLOY TUBING HANGER AND DUPLEX STAINLESS STEEL PIPING FAILURE INVESTIGATIONS

Product Number: 51300-03129-SG
ISBN: 03129 2003 CP
Author: S. Huizinga, B. McLoughlin, W.E. Liek, J.G. de Jong
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support