03118 INFLUENCE OF CHROMIUM CONTENTS OF 0.5 TO 1.0 % ON THE CORROSION BEHAVIOR OF LOW ALLOY STEEL FOR LARGE-DIAMETER PIPES IN CO2 CONTAINING AQUEOUS MEDIA

Picture for 03118INFLUENCE OF CHROMIUM CONTENTS OF
Available for download
Product Number: 51300-03118-SG
ISBN: 03118 2003 CP
Author: C. Bosch , J.-P. Jansen , R. K. Poepperling
$0.00
$20.00
$20.00
For investigation of the corrosion behavior of low alloy steels for large-diameter pipes for application in CO2 containing aqueous media, two alloy variations were produced as laboratory heats of 100 kg each, which contained 0.78 and 0.96 % Cr, respectively. Plates were rolled with a thickness of 20 mm and welded by use of two different chromium-free wires in order to investigate the corrosion behavior of the weld seam area. Furthermore, a segment of a large-diameter pipe with a chromium content of 0.59 % in the base material was included in the investigations. Laboratory tests were performed to determine the CO2 corrosion resistance in 0.1 % sodium chloride solution on flat specimens in the rotating cage under 1 bar (0.1 MPa) CO2 at 40, 70 and 90 °C and 1 m/s average flow velocity. The influence of an increased CO2 partial pressure of 30 bar (3.0 MPa) was investigated by use of rotating discs at 40 and 90 °C and 850 Rpm. The investigations revealed only a minor influence of the chromium content on the corrosion resistance. All specimens showed an improved resistance of the weld seams to CO2 corrosion compared to the base metals. The chromium contents added did not decisively improve the corrosion resistance of the steels.

Key Words: CO2 corrosion, low alloy steel, chromium, large-diameter pipe, flow, rotating cage, rotating disc, weld seam, corrosion rate
For investigation of the corrosion behavior of low alloy steels for large-diameter pipes for application in CO2 containing aqueous media, two alloy variations were produced as laboratory heats of 100 kg each, which contained 0.78 and 0.96 % Cr, respectively. Plates were rolled with a thickness of 20 mm and welded by use of two different chromium-free wires in order to investigate the corrosion behavior of the weld seam area. Furthermore, a segment of a large-diameter pipe with a chromium content of 0.59 % in the base material was included in the investigations. Laboratory tests were performed to determine the CO2 corrosion resistance in 0.1 % sodium chloride solution on flat specimens in the rotating cage under 1 bar (0.1 MPa) CO2 at 40, 70 and 90 °C and 1 m/s average flow velocity. The influence of an increased CO2 partial pressure of 30 bar (3.0 MPa) was investigated by use of rotating discs at 40 and 90 °C and 850 Rpm. The investigations revealed only a minor influence of the chromium content on the corrosion resistance. All specimens showed an improved resistance of the weld seams to CO2 corrosion compared to the base metals. The chromium contents added did not decisively improve the corrosion resistance of the steels.

Key Words: CO2 corrosion, low alloy steel, chromium, large-diameter pipe, flow, rotating cage, rotating disc, weld seam, corrosion rate
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03128 SELECTING MATERIALS FOR AN OFFSHORE
Available for download

03128 SELECTING MATERIALS FOR AN OFFSHORE DEVE LOPMENT CHARACTERIZED BY SOUR AND HIGH SALINITY ENVIRONMENT

Product Number: 51300-03128-SG
ISBN: 03128 2003 CP
Author: Ardjan Kopliku, Lucrezia Scoppio
$20.00
Picture for 03129 OFFSHORE NICKEL ALLOY TUBING HANGER
Available for download

03129 OFFSHORE NICKEL ALLOY TUBING HANGER AND DUPLEX STAINLESS STEEL PIPING FAILURE INVESTIGATIONS

Product Number: 51300-03129-SG
ISBN: 03129 2003 CP
Author: S. Huizinga, B. McLoughlin, W.E. Liek, J.G. de Jong
$20.00
Picture for 03316 CORROSION CONTROL STRATEGIES OF DOWNHOLE
Available for download

03316 CORROSION CONTROL STRATEGIES OF DOWNHOLE PUMPING EQUIPMENT AND FLOW LINES ON WELLS CONTAINING CO2/H2S USING RISK BASED ANALYSIS (RBA) TECHNIQUES

Product Number: 51300-03316-SG
ISBN: 03316 2003 CP
Author: Carlos A. Palacios T., Juan C. Martinez, Thais M. Hernández, Danielli Quintero
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support