01155 THE EFFECTS OF REACTIVE ELEMENT (Y, Hf) ADDITIONS ON THE ADHERENCE OF ALUMINA TO AN Fe-20Cr-4Al ALLOY WITH SULFUR

Picture for 01155 THE EFFECTS OF REACTIVE ELEMENT (Y, Hf)
Available for download
Product Number: 51300-01155-SG
ISBN: 01155 2001 CP
Author: K. Sasaki, T. Amano, N. Sakai and H. Isobe
$0.00
$20.00
$20.00
The effects of reactive element (10, 300 and 3700 ppmY, 500, 1900 and 4300 ppmHf) additions on the adherence of alumina to an Fe-20Cr-4A1 alloy with sulfur (185 ppmS) were studied in air or oxygen at 1373 K for 18, 360 and 1800 ks by mass-change measurements, X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). Oxide scales on the 185 ppmS and the 10 ppmY alloys spalled slightly after oxidation for 360 ks, and spalled from the entire surface after oxidation for 1800 ks. On the other hand, spalling of oxide scales from the other alloys practically did not occur after any oxidation time. Mass gains decreased for alloys with small additions of reactive elements, and then increased with increasing content of reactive elements. Oxide scales on the 185 ppmS alloy showed a slightly convoluted morphology, however, surface morphologies of oxide scales on the other alloys with reactive elements, except the 500 ppmHf, were almost planar after oxidation for 1800 ks.

Key Words: Oxide adherence, Alumina scale, Sulfur, Yttrium, Hafnium, Oxidation, Heat-resistant alloy, Chromium sulfide
The effects of reactive element (10, 300 and 3700 ppmY, 500, 1900 and 4300 ppmHf) additions on the adherence of alumina to an Fe-20Cr-4A1 alloy with sulfur (185 ppmS) were studied in air or oxygen at 1373 K for 18, 360 and 1800 ks by mass-change measurements, X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). Oxide scales on the 185 ppmS and the 10 ppmY alloys spalled slightly after oxidation for 360 ks, and spalled from the entire surface after oxidation for 1800 ks. On the other hand, spalling of oxide scales from the other alloys practically did not occur after any oxidation time. Mass gains decreased for alloys with small additions of reactive elements, and then increased with increasing content of reactive elements. Oxide scales on the 185 ppmS alloy showed a slightly convoluted morphology, however, surface morphologies of oxide scales on the other alloys with reactive elements, except the 500 ppmHf, were almost planar after oxidation for 1800 ks.

Key Words: Oxide adherence, Alumina scale, Sulfur, Yttrium, Hafnium, Oxidation, Heat-resistant alloy, Chromium sulfide
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 01149 OXIDATION OF IRON IN 288°C, OXYGEN-
Available for download

01149 OXIDATION OF IRON IN 288°C, OXYGEN-CONTAINING WATER

Product Number: 51300-01149-SG
ISBN: 01149 2001 CP
Author: Christopher S. Kumai and Thomas M. Devine
$20.00
Picture for 01144 CORROSION TESTING IN SUPPORT OF THE
Available for download

01144 CORROSION TESTING IN SUPPORT OF THE ACCELERATOR PRODUCTION OF TRITIUM PROGRAM

Product Number: 51300-01144-SG
ISBN: 01144 2001 CP
Author: G.T. Chandler, K.A. Dunn, M.R. Louthan, Jr., JT Mickalonis, F.D. Gac, S.A. Maloy, M.A. Paciotti, W.F
$20.00
Picture for 01146 INITIAL EVALUATION OF THE EFFECT
Available for download

01146 INITIAL EVALUATION OF THE EFFECT OF NEUTRON ABSORBERS ON THE CORROSION OF URANIUM-ALUMINUM ALLOYS

Product Number: 51300-01146-SG
ISBN: 01146 2001 CP
Author: D. W. Vinson, J. I. Mickalonis, and R. L. Sindelar
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support