99445 A HIGH STRENGTH AUSTENITIC MATERIAL, FULLY RESISTANT TO STRESS CORROSION CRACKING IN NUCLEAR ENVIRONMENTS

Product Number: 51300-99445-SG
ISBN: 99445 1999 CP
Author: Ruth Magdowski and Markus O. Speidel
$0.00
$20.00
$20.00
A face centered cubic chromium-based material has been observed to resist stress corrosion cracking in simulated reactor water, even in the cold worked, high strength condition. Strength levels up to 1100 MPa have been investigated in both PWR and BWR simulated reactor coolant. While all common nuclear structural materials have exhibited stress corrosion cracking in one or both of these environments, the new material remained free from stress corrosion crack growth. Testing was done with precracked fracture mechanics specimens. Keywords: Stress corrosion cracking, chromium based material, alloy 33, high strength.
A face centered cubic chromium-based material has been observed to resist stress corrosion cracking in simulated reactor water, even in the cold worked, high strength condition. Strength levels up to 1100 MPa have been investigated in both PWR and BWR simulated reactor coolant. While all common nuclear structural materials have exhibited stress corrosion cracking in one or both of these environments, the new material remained free from stress corrosion crack growth. Testing was done with precracked fracture mechanics specimens. Keywords: Stress corrosion cracking, chromium based material, alloy 33, high strength.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 00222 STRESS CORROSION CRACK GROWTH IN ALLOY
Available for download

00222 STRESS CORROSION CRACK GROWTH IN ALLOY 600 EXPOSED TO PWR AND BWR ENVIRONMENTS

Product Number: 51300-00222-SG
ISBN: 00222 2000 CP
Author: Markus O. Speidel and Ruth Magdowski
$20.00
Picture for 96112 EFFECT OF COLD WORK ON THE GROWTH
Available for download

96112 EFFECT OF COLD WORK ON THE GROWTH RATES OF STRESS CORROSION CRACKS IN STRUCTURAL MATERIALS OF NUCLEAR SYSTEMS

Product Number: 51300-96112-SG
ISBN: 96112 1996 CP
Author: Ruth Magdowski, Markus O. Speidel
$20.00
Picture for 96265 EFFECT OF TEMPERATURE ON CRACK GROWTH
Available for download

96265 EFFECT OF TEMPERATURE ON CRACK GROWTH RATES OF STRESS CORROS1ON CRACKS IN METAL ALLOYS EXPOSED TO WATER

Product Number: 51300-96265-SG
ISBN: 96265 1996 CP
Author: Helen Vogt, Markus 0. Speidel
$20.00