97117 EFFECTS OF ETA, PH CHANGE, AND INCREASED HYDRAZINE LEVELS ON DEPOSIT-COVERED ALLOY 600 AND BRASS CORROSION AT INDIAN POINT 2

Available for download

Product Number: 51300-97117-SG

ISBN: 97117 1997 CP

Author: Aaron Barkatt, Ewa Labuda, Donna M. Wilder, Susan Smialowska, Raul B. Rebak, Gahna Cherepakhov, Reyn

Member Price: $0.00

Non Member Price: $20.00

Price: $20.00

Qty:

Chemical dissolution tests and electrochemical tests were carried out on Alloy 600 specimens covered with synthetic deposit simulating the tube deposits in the steam generators at IndIao Point 2. The tests showed that the introduction of ETA and a moderate increase in pH gave rise to lower corrosion rates, but enhancement of hydrazine levels caused them to rise. In the case of brass, both types of tests showed that raisiig the pH caused the corrosion rates to increase, but the introduction of ETA led to mild decrease in these rates.

Overview

PRICE BREAKS - The more you buy, the more you save

Quantity

Price

$20.00

Product tags

Also Purchased

Available for download

Failures of Brass Components in Water and Steam Systems

Product Number: 51317--9123-SG

ISBN: 9123 2017 CP

Author: James Dillon

Publication Date: 2017

$20.00

Case histories will illustrate failures that occurred in components that were made of different brass alloys in water and steam systems. Recommendations will be made to mitigate the damage that occurred in each case.

Available for download

51318-11098- Microbial Assisted Cracking of Admiralty Brass Tubes from Lube Oil Cooler

Product Number: 51318-11098-SG

Author: Yousif Al Rabie / Khalid Al-Nabulsi / Faisal Al-Abbas

Publication Date: 2018

$20.00

This work investigates unexpected leaks observed on several cracked admiralty brass tubes that failed after 7 years in operation. Both metallurgical and molecular microbiological methods were used to understand the root cause of these failures.