03681 THE CORROSION OF MORE THAN 176 MILLION YEAR OLD NATIVE COPPER PLATES FROM A DEPOSIT IN MUDSTONE IN SOUTH DEVON; UNITED KINGDOM

Picture for 03681 THE CORROSION OF MORE THAN 176 MILLION
Available for download
Product Number: 51300-03681-SG
ISBN: 03681 2003 CP
Author: Antoni E. Milodowski, Michael T. Styles, Lars Werme, Virginia M. Oversby
$0.00
$20.00
$20.00
Copper is the selected material for the corrosion barrier in the canister for encapsulation of spent nuclear fuel from the Swedish power reactors. These canisters will be buried in a deep geological repository in granitic rock at a depth of 400 to 700 m. At these depths, the groundwater will be reducing and copper will be immune to corrosion in the absence of dissolved sulphides. Under these conditions the spent fuel canisters are expected to meet with a very high margin SKB’s design goal of 100 000 years. Extrapolations of short-term experimental data to such long times will always have some degree of uncertainty. Therefore, natural analogues are sometimes used to bridge the gap between laboratory time scales and the very long times for which a repository is designed. In the present paper, we present an analysis of the corrosion of native copper plates that have survived in a water-saturated clay environment for more than 176 million years. Although the native copper is affected by corrosion, the study shows that a significant proportion (30-80 % of the original thickness) of the copper sheets is preserved in the saturated compacted clay environment of the Littleham Mudstone. Apart from the recent weathering effects due to exposure at outcrop, petrographical studies demonstrate that most of the observed corrosion and alteration of the native copper is geologically old (i.e. predating the main sediment compaction) and also occurred before the end of the Lower Jurassic. This demonstrates that the native copper can remain stable in a saturated and compacted clay environment for geological timescales well in excess of the timescales considered for performance assessment of a deep geologic repository for spent nuclear fuel. Keywords: nuclear waste containers, copper, natural analogues, lifetime predictions.
Copper is the selected material for the corrosion barrier in the canister for encapsulation of spent nuclear fuel from the Swedish power reactors. These canisters will be buried in a deep geological repository in granitic rock at a depth of 400 to 700 m. At these depths, the groundwater will be reducing and copper will be immune to corrosion in the absence of dissolved sulphides. Under these conditions the spent fuel canisters are expected to meet with a very high margin SKB’s design goal of 100 000 years. Extrapolations of short-term experimental data to such long times will always have some degree of uncertainty. Therefore, natural analogues are sometimes used to bridge the gap between laboratory time scales and the very long times for which a repository is designed. In the present paper, we present an analysis of the corrosion of native copper plates that have survived in a water-saturated clay environment for more than 176 million years. Although the native copper is affected by corrosion, the study shows that a significant proportion (30-80 % of the original thickness) of the copper sheets is preserved in the saturated compacted clay environment of the Littleham Mudstone. Apart from the recent weathering effects due to exposure at outcrop, petrographical studies demonstrate that most of the observed corrosion and alteration of the native copper is geologically old (i.e. predating the main sediment compaction) and also occurred before the end of the Lower Jurassic. This demonstrates that the native copper can remain stable in a saturated and compacted clay environment for geological timescales well in excess of the timescales considered for performance assessment of a deep geologic repository for spent nuclear fuel. Keywords: nuclear waste containers, copper, natural analogues, lifetime predictions.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 03665 Combination of Cold Work and Heat Treatment
Available for download

03665 Combination of Cold Work and Heat Treatment on Stress Corrosion Cracking Susceptibility of L-grade Stainless Steel

Product Number: 51300-03665-SG
ISBN: 03665 2003 CP
Author: Yoshinori Katayama, Motoji Tsubota and Yoshiaki Saito
$20.00
Picture for 03675 The Effect of pH on Nickel Alloy SCC and
Available for download

03675 The Effect of pH on Nickel Alloy SCC and Corrosion Performance

Product Number: 51300-03675-SG
ISBN: 03675 2003 CP
Author: D.S. Morton, and M Hansen
$20.00
Picture for 03667 Electrochemical Mitigation of Intergranular
Available for download

03667 Electrochemical Mitigation of Intergranular Stress Corrosion Cracking in BWRs

Product Number: 51300-03667-SG
ISBN: 03667 2003 CP
Author: Young-Jin Kim
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support