51318-11090-The effect of corrosion product formation mode on the early stage of sour corrosion behavior on pipeline steel

Picture for The effect of corrosion product formation mode on the early stage of sour corrosion behavior on pipeline steel
Available for download

In this paper, the scaling mode at the early stage of carbon steel exposed to H2S environments with short exposure time were investigated. Corrosion exposure tests and linear polarization resistance (LPR) techniques were performed.

Product Number: 51318-11090-SG
Author: Huixin Li / Jiancang Liu / Lei Zhang / Zhu Wang / Fengxian Shi / Minxu Lu
Publication Date: 2018
Industry: Science of Corrosion
$0.00
$20.00
$20.00

The rapid process at the initial stage of sour corrosion on carbon steels and the relatively low uniform corrosion rate show the change of corrosion mechanism and the effect of corrosion products over time. In this paper, the scaling mode at the early stage of carbon steel exposed to H2S environments with short exposure time were investigated. Corrosion exposure tests and linear polarization resistance (LPR) techniques were performed. The corrosion products of pipeline steel formed under sour corrosion conditions were analyzed by scanning electron microscopy (SEM), and X-ray diffraction (XRD). Based on corrosion rate and the parameters of water chemistry, solubility limits of iron sulfide (FeS) were calculated. A preferred orientation of mackinawite appeared after 30 min of immersion. After exposure for one hour, the solution supersaturated and the corrosion product began to precipitate on the steel surface. Assuming the corrosion film covered the matrix layer by layer, the thickness of FeS were calculated based on water chemistry input. There was a significant difference between the calculated result and the film thickness of the cross-section. The corrosion product layers were loose and covered the matrix incompletely at the early stage of H2S corrosion. The rapidly scaling mode derived by the experiment and theoretical works is expected to improve the understanding of the mechanism of H2S corrosion at early stage and the possibility of the nucleation of the pitting under sour conditions.

Key words: Sour Corrosion, Corrosion product, Exposure time, Pipeline steel, Localized corrosion

The rapid process at the initial stage of sour corrosion on carbon steels and the relatively low uniform corrosion rate show the change of corrosion mechanism and the effect of corrosion products over time. In this paper, the scaling mode at the early stage of carbon steel exposed to H2S environments with short exposure time were investigated. Corrosion exposure tests and linear polarization resistance (LPR) techniques were performed. The corrosion products of pipeline steel formed under sour corrosion conditions were analyzed by scanning electron microscopy (SEM), and X-ray diffraction (XRD). Based on corrosion rate and the parameters of water chemistry, solubility limits of iron sulfide (FeS) were calculated. A preferred orientation of mackinawite appeared after 30 min of immersion. After exposure for one hour, the solution supersaturated and the corrosion product began to precipitate on the steel surface. Assuming the corrosion film covered the matrix layer by layer, the thickness of FeS were calculated based on water chemistry input. There was a significant difference between the calculated result and the film thickness of the cross-section. The corrosion product layers were loose and covered the matrix incompletely at the early stage of H2S corrosion. The rapidly scaling mode derived by the experiment and theoretical works is expected to improve the understanding of the mechanism of H2S corrosion at early stage and the possibility of the nucleation of the pitting under sour conditions.

Key words: Sour Corrosion, Corrosion product, Exposure time, Pipeline steel, Localized corrosion

Product tags
Also Purchased
Picture for The Application Limitation Boundary of Duplex Stainless Steel under Sour Condition in Oil Fields
Available for download

51318-11084-The Application Limitation Boundary of Duplex Stainless Steel under Sour Condition in Oil Fields

Product Number: 51318-11084-SG
Author: Ziru Zhang / Zhu Wang / Junpeng Xue / Lei Zhang / Xian Tang / Minxu Lu
Publication Date: 2018
$20.00

Pitting failure boundary of duplex stainless steel under sour condition was investigated by electrochemical and immersion tests. Polarization measurements investigate the effect of temperature and H2S on the corrosion behavior.
Picture for 51318-11098- Microbial Assisted Cracking of Admiralty Brass Tubes from Lube Oil Cooler
Available for download

51318-11098- Microbial Assisted Cracking of Admiralty Brass Tubes from Lube Oil Cooler

Product Number: 51318-11098-SG
Author: Yousif Al Rabie / Khalid Al-Nabulsi / Faisal Al-Abbas
Publication Date: 2018
$20.00

This work investigates unexpected leaks observed on several cracked admiralty brass tubes that failed after 7 years in operation. Both metallurgical and molecular microbiological methods were used to understand the root cause of these failures.
Picture for Electrochemical corrosion comparison of seamless tubes in UNS S31266 and UNS S31254
Available for download

51318-11092-Electrochemical corrosion comparison of seamless tubes in UNS S31266 and UNS S31254

Product Number: 51318-11092-SG
Author: Amelie Eriksson / Katarina Persson / Kristina Lund
Publication Date: 2018
$20.00

Critical pitting temperature (CPT) for UNS S31266 was compared to UNS S31254 with the newly developed electrochemical method, modified ASTMG150 developed by K. Lund et al., using 3M magnesium chloride (MgCl2) instead of 1M sodium chloride (NaCl).
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support